ZnO thin films on Si(1 1 1) grown by pulsed laser deposition from metallic Zn target

✍ Scribed by Jie Zhao; Lizhong Hu; Zhaoyang Wang; Jie Sun; Zhijun Wang

• Publisher: Elsevier Science
• Year: 2006
• Tongue: English
• Weight: 400 KB
• Volume: 253
• Category: Article
• ISSN: 0169-4332
• DOI: 10.1016/j.apsusc.2006.01.018

✦ Synopsis

ZnO thin films with highly c-axis orientation have been fabricated on p-type Si(1 1 1) substrates at 400 8C by pulsed laser deposition (PLD) from a metallic Zn target with oxygen pressures between 0.1 and 0.7 mbar. Experimental results indicate that the films deposited at 0.3 and 0.5 mbar have better crystalline and optical quality and flatter surfaces than the films prepared at other pressures. The full width at half maximum (FWHM) of (0 0 0 2) diffraction peak decreases remarkably from 0.46 to 0.198 with increasing annealing temperature for the film prepared at 0.3 mbar. In photoluminescence (PL) spectra at room temperature, the annealed film at 700 8C exhibits a smaller ultraviolet (UV) peak FWHM of 108 meV than the as-grown film (119 meV). However, an enhanced deep-level emission is observed. Possible origins to above results are discussed.