Solid oxide galvanic cells involving exchanged beta-alumina electrolyte

✍ Scribed by G. Róg; S. Koziński; A. Koz⇌owska-Róg

Publisher
Elsevier Science
Year
1981
Tongue
English
Weight
226 KB
Volume
26
Category
Article
ISSN
0013-4686

No coin nor oath required. For personal study only.

✦ Synopsis

Fe(II), Cu(I), Cu(II), and Zn(II)-exchanged beta-aluminas have been prepared and tested as solid electrolytesin oxide galvanic cells. The values offrec enthalpies ofFe,O,, CuCrO,, CuCr,O,, and Zn,SiO+ of formation at 1070 K have been calculated from the er# results. The reasonable agreement with literature data has been found for all compounds under study

📜 SIMILAR VOLUMES

Calcium-beta″-alumina: Preparation, prop
Calcium-beta″-alumina: Preparation, properties and application to the solid oxide galvanic cells
✍ G. Róg; W. Pycior; K. Zakuła; A. Kozłowska-Róg; M. Bućko 📂 Article 📅 1993 🏛 Elsevier Science 🌐 English ⚖ 451 KB

Ahatract-Calcium-beta"-almina was prepared by ion exchange in an appropriate molten salt. It appeared to be practically pure beta"-AI,O,. The ionic conductivity was measured using molten salt electrodes and by a complex impedance analysis using platinum electrodes. The electronic conductivity was de

Determination of the standard molar Gibb
Determination of the standard molar Gibbs energy of formation of lanthanum zirconate by a galvanic cell involving lanthanum β-alumina electrolyte
✍ G. Róg; A. Kozłowska-Róg 📂 Article 📅 2002 🏛 Elsevier Science 🌐 English ⚖ 55 KB

The standard molar Gibbs energy of formation of La 2 Zr 2 O 7 from La 2 O 3 and ZrO 2 has been determined in the temperature range 1073 K to 1273 K by the e.m.f. measurements. The solid-state galvanic cell involving lanthanum β-alumina electrolyte was applied. The average values of the standard enth

Determination of the standard molar Gibb
Determination of the standard molar Gibbs energy of formation of calcium zirconate by a galvanic cell involving calcium-ion conducting solid electrolyte
✍ G. Róg; M. Potoczek-Dudek 📂 Article 📅 2001 🏛 Elsevier Science 🌐 English ⚖ 69 KB

The standard molar Gibbs energy of formation of CaZrO 3 from CaO and ZrO 2 has been determined by the e.m.f. measurements of a galvanic cell with calcium-ion conducting solid-state electrolyte in the temperature range 1073 K to 1273 K. The average values of the standard enthalpy and the standard ent