Tensile tests on Ni, (AI\*Ti) single crystals were carried out to elucidate the mechanism of the positive temperature dependence of the work hardening rate and CRSS as a function of orientation below room temperature. The increment of the maximum work hardening rate 0," is satisfactorily expressed o
The crystallography of the cubic-to-monoclinic stress-induced martensitic transformation in a Ti49.8at%Ni alloy was studied using single crystals. Experimental results were compared with predictions of phenomenological crystallographic theory. Simultaneously, we measured most of the usual crystallog
Forsterite monocrystals doped with Ti and Ni were grown by the flux growth technique. A suitable mixture of flux (MoO 3 , V 2 O 5 , Li 2 CO 3 ) and nutrient was slowly cooled down to 750 Β°C from 1250 Β°C or 1350 Β°C. The crystals were then characterized by powder and single-crystal X-ray diffraction,