The crystallography of the cubic-to-monoclinic stress-induced martensitic transformation in a Ti49.8at%Ni alloy was studied using single crystals. Experimental results were compared with predictions of phenomenological crystallographic theory. Simultaneously, we measured most of the usual crystallographic parameters: habit plane, orientation relationship, magnitude and direction of shape strain. With some deviations, for {0.72053, 1, I}(Olf) Type 11 twinning, we found consistency between theory and experiment for all the parameters, A possible origin for the deviations is also discussed.R&sum&-Nous avons itudik sur des monocristaux la cristallographie de la transformation de phase martensitique~ de cubique en manoclinique, induite par la contrainte dans un al&age de titane $49,8 at.% de nickel. Nous avons cornpark les r&sultats exp~rimentaux avec les p&visions d'une thtorie cristallographique ph~nom~nologique. Simultan~ment, nous avons mesurk la plupart des paramgtres cristallographiques usuels: plan d'accolement, relation d'orientation, grandeur et direction de la diformation de .forme. Avec quelques &carts, nous avons trot& pour le maclage de type II (0.72053, 1, I i(OlT) un accord entre la thkorie et l'experience pour tous les paramitres. Nous discutons tgalement une origine possible des icarts.Zusammenfassung-An Einkristallen der Legierung Ti49.8 At.-% Ni wurde die Kristallographie der spannungsinduzierten martensitischen Umwandlung kubisch zu monoklin untersucht. Die experimentellen Ergebnisse wurden mit Voraussagen der phgnomenologischen kristallographischen Theorie verglichen. Gleichzeitig ermittelten wir die meisten der iiblichen kristallographischen Parameter: Habitebene, Orietierungszusammenhang, Gr613e und Richtung der Formverzerrung. Mit einigen Abweichungen, beim {0,72053, 1. 1) (017) Typ-II-Zwilling, waren Theorie und Experiment vertrgglich miteinander. Eine miigliche Ursache fiir die Abweichungen wird auBerdem betrachtet.