Microstructure and associated properties of YBCO superconductors prepared by melt-processing techniques

✍ Scribed by U. Balachandran; W. Zhong; C. A. Youngdahl; R. B. Poeppel

Book ID
112901613
Publisher
Springer US
Year
1993
Tongue
English
Weight
970 KB
Volume
22
Category
Article
ISSN
0361-5235

No coin nor oath required. For personal study only.

πŸ“œ SIMILAR VOLUMES

Processing and characterization of YBCO
Processing and characterization of YBCO superconductors by top-seeded melt growth method in batch process
✍ H.T. Ren; L. Xiao; Y.L. Jiao; M.H. Zheng πŸ“‚ Article πŸ“… 2004 πŸ› Elsevier Science 🌐 English βš– 299 KB

Single domain superconducting YBCO disks up to 30-50 mm in diameter have been prepared in batch process. A box furnace or a well-styled furnace was used in the processing. High oxygen pressure (up to 2 MPa) annealing of the samples was used in the final treatment. The levitation forces for 30 mm in

The microstructure and superconducting p
The microstructure and superconducting properties of melt-processed YBCO samples containing RE-211 particles
✍ Y. Yanagi; Y. Itoh; M. Yoshikawa; T. Oka; M. Sasaki; Y. Yamada; U. Mizutani πŸ“‚ Article πŸ“… 1994 πŸ› Elsevier Science 🌐 English βš– 156 KB

The melt-processed YBCO containing rare-earth 211-particles (Yb2BaCuOs) were synthesized with or without Pt-doping. A mixing of Yb and Y in the 211-phase occurs immediately after the incongruent melting of the 123-phase and proceeds during solidification. However, Pt-doping is found to suppress subs