It is found that small amounts of plastic deformation greatly enhance the rate of annealing in gold quenched from 700Β°C. It is found that the activation energy of motion before deformation is 0.82 eV, whereas after deformation it is 0.64 f 0.03 eV. Using the theory of Cochardt et &.'*I it is shown that this change can be understood by supposing that near a dislocation lattice vacancies prefer to exist as divacancies, since as divacancies there is a larger attractive interaction. The possibility of trapping defects of low symmetry near dislocations is discussed. INFLUENCE DE LA DEFORMATION PLASTIQUE SUR LE RECUIT DE L'OR APRES TREMPE De faibles pourcentages de dhformation plastique ralentissent fortement la vitessee de recuit de l'or trempb it partir de 700Β°C. L'Qnergie d'activation qui, avant la deformation est de 0.82 eV, est devenue apr&s 0.64 f 0.03 eV. En utilisant la thborie de Cochardt et al., i2) les auteurs montrent que cette modification peut s'interpr&er en admettant qu'au voisinage d'une dislocation du rbseau, les lacunes existent pr&f&entiellement par paire: en effet, dans cette disposition il existe une interaction attractive plus BlevCe. Enfin, l'attraction des defauts de faible sym&rie par les dislocations, est envisagbe. EINFLUD PLASTISCHER VERFORMUNG AUF DIE ERHOLUNG VON ABGESCHRECKTEM GOLD Schon geringe plastische Verformungen beschleunigen die Erholung von Gold, das von 700Β°C abgeschreckt wurde, sehr. Vor der Verformung ist die Wanderungsenergie 0.82 eV, nach der Verformung 0.64 & 0.03 eV. Mit Hilfe der Theorie von Cochardt u.a.'2) wird gezeigt, daIj dieser Wandel auf Grund der Annahme verstanden werden kann, daO in der N&he einer Versetzung die Leerstellen vorzugweise als Doppelleerstellen existieren; ftir Doppelleerstellen ist niimlich die anziehende Wechselwirkung grdDer. Die MGglichkeit, dal3 Defekte mit niedriger Symmetric in der N&he von Versetzungen eingefangen werden, wird diskutiert.