Effect of loading history on stress corrosion cracking in high strength steel

✍ Scribed by Y. Hirose; T. Mura

Publisher: Elsevier Science
Year: 1984
Tongue: English
Weight: 754 KB
Volume: 3
Category: Article
ISSN: 0167-6636
DOI: 10.1016/0167-6636(84)90001-2

No coin nor oath required. For personal study only.

📜 SIMILAR VOLUMES

Stress corrosion crack branching in high

Stress corrosion crack branching in high-strength steels

✍ C.S. Carter 📂 Article 📅 1971 🏛 Elsevier Science 🌐 English ⚖ 811 KB

The criteria for stress corrosion crack branching in high-strength steels are shown to be (1) a constant crack velocity and (2) attainment of a critical stress intensity Klb. For the steels investigated, values of K,b I K,,,, range from 2 to 4. This indicates that when K,, /K,, exceeds 0.5, rapid br

Mechanism of corrosion fatigue crack pro

Mechanism of corrosion fatigue crack propagation in high strength steels

✍ Nakasa Keijiro; Takei Hideo; Itoh Hisashi 📂 Article 📅 1983 🏛 Elsevier Science 🌐 English ⚖ 922 KB

The crack propagation velocity in corroGon fatigue (du/dN), were measured on the Ni-Cr-Mo steel quenched and tempered at 473 or 773 K. The steel with high sensitivity to delayed failure reveals the largest (du/dN), under square load and the smaller (da/dN), under positive saw tooth load. The frequen

Crack nucleation and propagation of corr

Crack nucleation and propagation of corrosion fatigue in high-strength steel

✍ Y Hirose; T Mura 📂 Article 📅 1985 🏛 Elsevier Science 🌐 English ⚖ 851 KB

Crack nucleation and growth behavior of corrosion fatigue are investigated experimentally and theoretically for 200°C tempered AISI 4340 steel in 35% NaCl solution. The crack nucleation at notch roots is determined by the electrical potential method. The cycle for crack nucleation, N,, increases wit

The effect of loading pattern on the gro

The effect of loading pattern on the growth rate of a stress corrosion crack at high stress levels

✍ E. Smith 📂 Article 📅 1984 🏛 Elsevier Science ⚖ 577 KB

The effect of shot peening on stress cor

The effect of shot peening on stress corrosion cracking behaviour of 2205-duplex stainless steel

✍ Y.F. Al-Obaid 📂 Article 📅 1995 🏛 Elsevier Science 🌐 English ⚖ 509 KB

In this paper an attempt has been made to study the effect of shot peening on stress corrosion cracking of 2205-Duplex stainless steel. Cast steel shot was selected to be the peening media. Specimens of 2205-Duplex stainless steel were tested in the peened and unpeened condition. Quantitative data o

Effect of loading condition on very high

Effect of loading condition on very high cycle fatigue behavior in a high strength steel

✍ Masaki Nakajima; Keiro Tokaji; Hisatake Itoga; Toshihiro Shimizu 📂 Article 📅 2010 🏛 Elsevier Science 🌐 English ⚖ 588 KB

Very high cycle fatigue tests were conducted under rotating bending and axial loading using a high carbon chromium steel, JIS SUJ2, in order to evaluate the effect of loading condition on subsurface fracture with a fish-eye. In very high cycle region where subsurface crack was generated at a non-met