Corrosivity of Br− and Cl− on duplex stainless steel

✍ Scribed by Katsumi Yamamoto; Keizo Hosoya

Publisher
Elsevier Science
Year
1995
Tongue
English
Weight
385 KB
Volume
198
Category
Article
ISSN
0921-5093

No coin nor oath required. For personal study only.

✦ Synopsis

This report discusses the basis for material selection in chemical plants, especially focusing on the design of an actual plant based on laboratory corrosion test results. Both the chemical system created when chlorine gas and bromine gas were neutralized with alkaline solution, and material economics are considered when selecting duplex stainless steel as a construction material.

In addition, the corrosivity of Br-and CI-with or without BrO-and CIO-on duplex stainless steel is discussed in terms of pitting and crevice corrosion. Br-ions show a lower tendency to promote pitting and crevice corrosion on duplex stainless steel, compared with C1-ions. BrO-, existing in a bromine gas neutralization system, acts as a strong oxidizer and easily shifts the corrosion potential of duplex stainless steel more noble, drastically promoting crevice corrosion.

📜 SIMILAR VOLUMES

Corrosion resistance of low-nickel duple
Corrosion resistance of low-nickel duplex stainless steel rebars
✍ L. Bertolini; M. Gastaldi 📂 Article 📅 2010 🏛 John Wiley and Sons 🌐 German ⚖ 988 KB

## Abstract The use of stainless steel bars in reinforced concrete structures may be an effective method to prevent corrosion in aggressive environments where high amounts of chlorides may penetrate in the concrete cover. For an estimation of the service life of structures where stainless steel bar

Field and laboratory experiences of Sulf
Field and laboratory experiences of Sulfide stress corrosion of a duplex stainless steel
✍ Bruno Bazzoni; Alberto Cigada; Luciano Lazzari; Pietro Pedeferri 📂 Article 📅 1985 🏛 John Wiley and Sons 🌐 German ⚖ 745 KB

Targets of this work have been: testing of duplex stainless steel in field (into a geothermal well) and in laboratory NACE environment in presence of crevices and sharp defects; development of testing based on fracture mechanics and comparison with traditional testing approach. The following types

Electrolytic pickling of duplex stainles
Electrolytic pickling of duplex stainless steel
✍ N. Ipek; B. Holm; R. Pettersson; G. Runnsjö; M. Karlsson 📂 Article 📅 2005 🏛 John Wiley and Sons 🌐 German ⚖ 834 KB

## Abstract Pickling of duplex stainless steels has proved to be much more difficult than that of standard austenitic grades. Electrolytic pre‐pickling is shown to be a key process towards facilitating the pickling process for material annealed both in the production‐line and in laboratory experime