Transport critical current density of melt-processed (QMG) YBa2Cu3Ox bulk superconductors

✍ Scribed by K. Kimura; M. Morita; M. Tanaka; S. Takebayashi; L. Trouilleux; K. Miyamoto; M. Hashimoto; K. Watanabe; S. Awaji; N. Kobayashi

Publisher: Elsevier Science
Year: 1993
Tongue: English
Weight: 305 KB
Volume: 33
Category: Article
ISSN: 0011-2275
DOI: 10.1016/0011-2275(93)90244-i

No coin nor oath required. For personal study only.

✦ Synopsis

Transport critical currents of melt-processed (QMG) YBa2Cu3Ox bulk superconductors were measured by a d.c. four probe method. The QMC bulk specimens have high Jc characterisics of = 1 x 104 A cm-2 at 5 T for the magnetic field parallel to a-b plane. The angular dependence of Jo upon the direction of applied magnetic field showed some characteristic features which could not be described by simple flux pinning. This indicates that anisotropic pinning is relatively strong. The pinning caused by the layered structure, twin boundaries and oxygen deficiency, as well as pinning by the Y2BaCuOs phase, play important roles in determining the Jc of the QMG YBa2Cu30 x bulk superconductors.

📜 SIMILAR VOLUMES

Enhancement of critical current density

Enhancement of critical current density in fast neutron irradiated melt-textured YBa2Cu3O7-x

✍ R. Puźniak; A. Wiśniewski; M. Baran; H. Szymczak; Zhang Pingxiang; Wang Jingrong 📂 Article 📅 1993 🏛 Elsevier Science 🌐 English ⚖ 447 KB

The critical current density in melt-textured samples obtained by the powder melting process was determined from magnetization measurements. Linear dependence between the width of the hysteresis loop and sample size was observed for both unirradiated and irradiated samples. This indicates that the c

Influence of twinning and grain structur

Influence of twinning and grain structure on the critical transport current density of YBa2Cu3O7-δ

✍ S. Iwama; P.J. King; D.S. Misra; W.B. Roys; D.N. Matthews; K.N.R. Taylor 📂 Article 📅 1988 🏛 Elsevier Science 🌐 English ⚖ 260 KB

Optmal mmroscopy studies have been camed out to study the effect of twinning on the superconducting properties of bulk YBa2Cu307 ~ (1 2 3) using a range of samples which have been prepared under different condtttons of temperature and pressure m the authors' laboratories and elsewhere Although the p

Influence of fast neutron irradiation on

Influence of fast neutron irradiation on critical currents and irreversibility lines in MPMG-processed YBa2Cu3O7 superconductors

✍ M Wacenovsky; R Miletich; H.W Weber; M Murakami 📂 Article 📅 1993 🏛 Elsevier Science 🌐 English ⚖ 595 KB

## Research Melt-powder melt-grown samples with different amounts of artificially introduced 211 particles were exposed to fast neutron irradiation up to a fluence of 4 x 1021 m -2 (E > 0.1 MeV). The influence of the irradiation on the critical current characteristics and on the irreversibility li

Theoretical estimate of critical transpo

Theoretical estimate of critical transport current density in polycrystalline oxide superconductors

✍ T. Matsushita; B. Ni; K. Yamafuji 📂 Article 📅 1989 🏛 Elsevier Science 🌐 English ⚖ 353 KB

Percolative critical transport current densities in polycrystalline high T c oxide superconductors with orientated and random textures are theoretically estimated at the liquid nitrogen temperature. The effect of depression of the current through grain boundaries recently found by Dimos et al. was t

Preparation and critical current density

Preparation and critical current density of melt-processed YBaCuO thick films and AgPd-sheathed tapes

✍ K Fischer; G Leitner; G Fuchs; M Schubert; B Schlobach; A Gladun; C Rodig 📂 Article 📅 1993 🏛 Elsevier Science 🌐 English ⚖ 768 KB

Thermal analysis by differential scanning calorimetry (DSC) has shown that melting of YBa2Cu30 x is completed at 1000-1010°C in a nitrogen atmosphere. The N 2 can be exchanged by 02 without solidification of the melt and the solidification starts in 02 below 1000°C in the supercooled melt• Applying