Thermodynamic
properties of the silver-mercury and gold-mercury f.c.c. solid solutions have been determined using an isopiestic technique, the equilibrium compositions of the alloys being mainly obtained by X-ray analysis.
Dilute solutions in the two systems have similar entropies and may be "regular".
Excess entropies occur in the mercury-rich gold-mercury solutions.
Integral heats of
solution for the gold-mercury system are parabolically related to composition throughout the solid solution range, but for silver-mercury alloys the relationship is more complicated, as shown by the partial heat curves. Partial heats of solution of liquid mercury in solid silver and gold at infinite dilution are -4.05 and -2.19 kcal/g atom, respectively. The magnitudes of the heats of solution for silver-mercury and gold-mercury are discussed and compared with those in closely related systems. The present data are used to evaluate conflicting results regarding the position of the solidus in the silver-mercury equilibrium diagram. THERMODYNAMIQUE DES SOLUTIONS SOLIDES DU MERCURE DANS L'ARGENT ET L'OR Les auteurs ont determine a l'aide d'une technique isopiestique les proprietes thermodynamiques des solutions solides c.f.o. Argent-Mercure et Or-Mercure. Les compositions a l'equilibre ont ete principalement determinees par rayons X. Dans les deux systemes, les solutions diluees ont des entropies semblables et peuvent 6tre consider&es comme ideales. Les solutions Or-Mercure, riches en mercure, possedent des entropies en exces. Pour le systeme or-mercure, lea chaleurs totales de dissolution varient paraboliquement avec la composition dans tout le domaine de la solution solide. Pour les alliages argent-mercure, la relation est plus complexa, ainsi que le montrent les courbes de chaleur partielle. Les chaleurs partielles de dissolution du mercure liquide dans I'argent et dans l'or sont respectivement de -4,05 et -2,19 Kcal/at.gr. Les auteurs discutent et comparent les valeurs des chaleurs de dissolution des systemes argent-mercure et or-mercure avec celles de systemes analogues. Enfin, les resultats de cette etude permettent la critique des differentes positions du solidus du diagramme srgent-mercure fournies par la litterature. DIE THERMODYNAMIK DER FESTEN L&SUNG VON QUECKSILBER IN SILBER UND GOLD Die thermodynamischen Eigenschaften fester kubisch-flaohenzentrierter Liisungen von Quecksilber in Silber und Gold wurden gemessen, dabei wurden die Gleichgewichtszusammensetzungen hauptsachlich rontgenographisch ermittelt. Die verdiinnten Losungen beider Systeme haben ahnliche Entropien und konnen "regular" sein. Uberschuljentropien treten bei quecksilberreiohen Gold-Quecksilber-Legierungen auf. Die integralen Losungswarmen im Gold-Quecksilber-System hangen im ganzen Ibslichkeitsbereich parabolisch von der Zusammensetzung ab, wahrend bei Silber-Quecksilber-Legierungen der Zusammenhang komplizierter ist, wie die Kurven der partiellen Losungswarmen zeigen. Die partiellen Losungswarmen von fliissigem Quecksilber in festem Silber und Gold betragen bei unendlicher Verdunnung -4,05 bzw. -2,19 Kcal/gAtom. Die GrGBenordnungen der Losungswarmen bei Silber-Quecksilber und Gold-Quecksilber werden diskutiert und mit denen in verwandten Systemen vergliohen. Die vorliegenden Daten werden verwendet, urn zwischen widerspriichlichen Ergebnissen iiber die Lage der Soliduslinie im Silber-Quecksilber-Gleichgewichtsdiagramm zu entscheiden.