The enthalpies of formation at 640ยฐC of solid Ni-Cu and Ni-Au alloys have been measured as a function of composition by means of a differential solution calorimeter. Both systems are characterized by positive heats of formation. The conoentration variations of the partial molar heats of solution of Cu and of Ni in liquid Sn at 640ยฐC have been explored. It is shown that Cu in Sn does not satisfy the requirements of the quasi chemical theory, whereas Ni in Sn does so within experimental uncertainty. LES CHALEURS DE FORMATION DES ALLIAGES CUIVRE-NICKEL ET OR-NICKEL Los enthalpies de formation it 640ยฐC des &ages solides de cuivre-nickel et d'or-nickel ont et& mosurees en fonction de la composition it I'aida d'un ealorimetre differentiel. Les deux systemes sent caracterises par des chafeurs de formations positives. Les auteurs ont Bgalement examine les variations, des chaleurs partielles molaires de solution du cuivre et du nickel dans l'etain liquid0 a 640ยฐC en fonction de la concentration. 11s ont montre que pour le ouivre ces variations ne sat&font pas aux oxigences de la theorie quasi chimique tandis que celles du nickel dans l'etain y repondent bien, compte term des erreurs experimentales. WARMETONUNGEN VON NICKEL-KUPFER UND NICKEL-GOLD MISCHKRISTALLEN Die Bildungsenthalpien von Ni-Cu und Ni-Au Mischkristallen wurden bei 64O'C als Funktion der Zusammensetzung mit Hilfe sines differentiellen LBsungskalorimeters gomessen. Beide Systeme weisen eine positive Bildungswarme auf. Die Andernugen der partiellen molaren Lasungswiirmen van Cu und Ni in fltissigem Sn bei 640ยฐC wurdan in Abhlingigkeit von der Konxentration untersucht. Es zeigt sick, dass Cu in Sn die Forderungen der quasiohemischen Theorie nicht erfiillt, wilhrend diese bei Ni in Sn innerhalb der experimentellen Unsicherheiten erftillt sind.