The irradiation of CuAu with neutrons causes two separable effects. Disordering is caused by fast neutrons, and is negligible with thermal neutrons; the rate is approximately 0.7 of the rate for Cu3.4~. A secondary effect, probably ordering, is caused by thermal neutrons, very likely through the agency of the mercury formed, as with CulAu. The effect is much more pronounced with Cu.411 than with CuaAu, probably owing to the fact that the initial "freezing in" temperature is about 80Β°C instead of 200Β°C. LES EFFETS D'IRRADIATION AVEC DES NEUTRONS DANS LE Rl?ACTEUR KRX SUR LA TRANSFORMATION ORDRE-Dl%ORDRE D.4NS L'ALLIAGE CuAu L'irradiation de CuAu avec des neutrons cause deux effets s¶bles. Les neutrons rapides causent une mise en d&ordre; la vitesse est approximativement 0,7 de la vitesse dans le cas de Cu3.4~. Les neutrons thermiques causent un effet secondaire, probablement une mise en ordre, en toute vraisemblance par l'intermediaire du m&cure form& comme dans le cas de Cu3Au. Cet effet est beaucoup plus prononc6 dans le cas de CuAu que dans celui de Cu3Au, probablement g cause du fait que la tempCrature de "cong&ation" est d'environ 80Β°C au lieu de 200Β°C. DIE WIRKUNG VON NEUTRONENBESTRAHLUNG IM i;RX REACTOR AUF DEB ORDNUNGSGRAD VON CuAu Die Bestrahlung von CuAu mit Neutronen fiihrt zu zwei verschiedenen Effekten. Schnelle Neutronen fiihren eine Verminderung der Ordnung herbei; bei thermischen Neutronen kann dieser Effekt vernachl%ssigt werden. Die Geschwindigkeit ist etwa 0,f der Geschwindigkeit der Reaktion C~3~4u. Ein sekundgrer Effekt, wahrscheinlich Ordnen, wird durch thermische Neutronen hervorgerufen, sicher auf dem Umweg iiber das gebildete Quecksilber wie im Falle Cu3Au. Dieser Effekt ist im CuAu sehr viel stgrker als im Cu3.4~1, wahrscheinlich weil die "Einfrierungstemperatur" hier etwa 80Β°C im Gegensatz zu 200Β°C ist.