The effect of recrystallization on corrosion and electrochemical behavior of 7150 Al alloy

✍ Scribed by G. S. Peng; K. H. Chen; H. C. Fang; S. Y. Chen; H. Chao

Publisher
John Wiley and Sons
Year
2009
Tongue
German
Weight
848 KB
Volume
62
Category
Article
ISSN
0947-5117

No coin nor oath required. For personal study only.

✦ Synopsis

Abstract

By weight loss, potentiodynamic polarization, cyclic voltammetry, and electrochemical impedance spectroscopy (EIS) techniques complemented by optical and scanning electron microscopy observations, the effect of recrystallization on the corrosion, and electrochemical behavior of 7150 Al alloy was studied. The results indicated that the high recrystallization fraction 7150‐1# was worse than the low recrystallization fraction 7150‐2# on corrosion resistance. The analysis of EIS indicated that 7150‐1# exhibited obvious pitting corrosion at 5 h immersion time, whereas 7150‐2# showed no obvious pitting corrosion even at 33 h. The corrosion route developed along the grain boundary of recrystallization grains, not along the grain boundary of unrecrystallization grains.

πŸ“œ SIMILAR VOLUMES

Exfoliation corrosion of 7150 Al alloy w
Exfoliation corrosion of 7150 Al alloy with various tempers and its electrochemical impedance spectroscopy in EXCO solution
✍ J. F. Li; Z. Q. Jia; C. X. Li; N. Birbilis; C. Cai πŸ“‚ Article πŸ“… 2009 πŸ› John Wiley and Sons 🌐 German βš– 858 KB

## Abstract The exfoliation corrosion susceptibility and electrochemical impedance spectroscopy (EIS) of 7150 Al alloys with T6, T73, and RRA (retrogression at 175 °C for 3 h) tempers in EXCO solution were investigated. The anodic equilibrium precipitate __Ξ·__(MgZn~2~) is continuous or closely spac

Study on the effect of corrosion on the
Study on the effect of corrosion on the tensile behavior of an AZ91 alloy
✍ Q. Wang; Y. H. Liu; L. N. Zhang; Y. L. Song; D. W. Zhang; C. F. Li πŸ“‚ Article πŸ“… 2010 πŸ› John Wiley and Sons 🌐 German βš– 564 KB

## Abstract The effect of corrosion on the tensile behavior of an as‐cast AZ91 alloy was investigated via systematical experiments. The corrosion residual strength of the AZ91 magnesium alloy is approximately negative linear dependent on the extreme depth of corrosion pit, which was quantitatively

Electrochemical corrosion behavior of Al
Electrochemical corrosion behavior of Al–Si alloy composites reinforced with in situ TiB2 particulate
✍ H. H. Sun; D. Chen; X. F. Li; N. H. Ma; H. W. Wang πŸ“‚ Article πŸ“… 2009 πŸ› John Wiley and Sons 🌐 German βš– 431 KB

## Abstract Understanding the corrosion behavior of TiB~2p~‐reinforced aluminum matrix composites is crucial for their development as effective composites. In this work, corrosion characteristics of in situ TiB~2~ particulate reinforced Al–Si alloy (A356) composite after T6 treatment are investigat

EIS study on pitting corrosion of 7150 a
EIS study on pitting corrosion of 7150 aluminum alloy in sodium chloride and hydrochloric acid solution
✍ G. S Peng; K. H. Chen; H. C. Fang; H. Chao; S. Y. Chen πŸ“‚ Article πŸ“… 2010 πŸ› John Wiley and Sons 🌐 German βš– 581 KB

## Abstract The pitting corrosion behavior of 7150 aluminum alloy was studied by electrochemical impedance spectroscopy (EIS) in the sodium chloride and hydrochloric acid solution. Based on EIS features and corrosion morphologies as well as corrosion potential, the process of pitting corrosion coul