The effect of corrosion inhibiting pigments on environmentally assisted cracking of high strength aluminum alloy

✍ Scribed by X.F. Liu; S.J. Huang; H.C. Gu

Book ID: 117086039
Publisher: Elsevier Science
Year: 2003
Tongue: English
Weight: 292 KB
Volume: 45
Category: Article
ISSN: 0010-938X
DOI: 10.1016/s0010-938x(03)00025-8

No coin nor oath required. For personal study only.

📜 SIMILAR VOLUMES

Environmentally assisted crack growth ra

Environmentally assisted crack growth rates of high-strength aluminum alloys

✍ Brain J. Connolly; Kristen L. Deffenbaugh; Angela L. Moran; Michelle G. Koul 📂 Article 📅 2003 🏛 The Minerals, Metals & Materials Society 🌐 English ⚖ 663 KB

A critical evaluation of the stress-corr

A critical evaluation of the stress-corrosion cracking mechanism in high-strength aluminum alloys

✍ Lee, Seong-Min ;Pyun, Su-Il ;Chun, Young-Gab 📂 Article 📅 1991 🏛 The Minerals, Metals & Materials Society 🌐 English ⚖ 977 KB

The effect of loading mode on the stress

The effect of loading mode on the stress-corrosion cracking of aluminum alloy 5083

✍ Pickens, J. R. ;Gordon, J. R. ;Green, J. A. S. 📂 Article 📅 1983 🏛 The Minerals, Metals & Materials Society 🌐 English ⚖ 978 KB

Influence of corrosion inhibitors on the

Influence of corrosion inhibitors on the polarization effect during stress-corrosion cracking of aluminum alloy V95

✍ N. I. Narushevich; S. A. Balezin; V. V. Romanov 📂 Article 📅 1967 🏛 Springer 🌐 English ⚖ 132 KB

Effect of preliminary corrosion on the f

Effect of preliminary corrosion on the fatigue strength of an aluminum alloy D16

✍ A. V. Karlashov; A. D. Gnatyuk; N. F. Voronkin 📂 Article 📅 1968 🏛 Springer 🌐 English ⚖ 299 KB

The effect of D2O on fatigue-crack propa

The effect of D2O on fatigue-crack propagation in a high-strength aluminum alloy

✍ R. P. Wei; J. D. Landes 📂 Article 📅 1969 🏛 Springer Netherlands 🌐 English ⚖ 178 KB

The rates of fatigue-crack propagatmn for a h~gh-strength aluminum alloy (7075-T651) in a~ envaronment of D20 (99 98~ purity) at room temperature were determined and compared with data obtained in [ugh-purity argon and dastflled water. The results showed that D20 caused a ten-fold Increase in the ra