Influence of corrosion inhibitors on the polarization effect during stress-corrosion cracking of aluminum alloy V95

✍ Scribed by N. I. Narushevich; S. A. Balezin; V. V. Romanov

Publisher
Springer
Year
1967
Tongue
English
Weight
132 KB
Volume
2
Category
Article
ISSN
1573-885X

No coin nor oath required. For personal study only.

πŸ“œ SIMILAR VOLUMES

An ambiguity of the cathodic polarizatio
An ambiguity of the cathodic polarization effect on crack growth during stress corrosion cracking of aluminum alloys
✍ V. A. Marichev πŸ“‚ Article πŸ“… 1983 πŸ› John Wiley and Sons 🌐 German βš– 652 KB

## Abstract The kinetics of crack growth under the conditions of stress corrosion cracking of aluminum alloys in electrolytes with different anion composition and pH values from 0 to 13 has been studied. It is shown that for the majority of alloy‐electrolyte systems anodic polarization accelerates

Anion effects on the stress corrosion cr
Anion effects on the stress corrosion cracking behaviour of aluminium alloys
✍ R. Braun πŸ“‚ Article πŸ“… 2003 πŸ› John Wiley and Sons 🌐 German βš– 789 KB

The stress corrosion cracking behaviour of plate material of the aluminium alloys 2024-T351, 8090-T8171, 7475-T651, and 7075-T7351 was investigated performing constant load tests. Short transverse tensile specimens were permanently immersed in aerated aqueous 0.6 M Na 2 Cl solutions with additions o