Kinetic and crystallographic observations on the natural and stress-induced transformations in single crystals of cobalt and cobalt-nickel alloys have oonhrmed the martensitic nature of the change. The shape deformation has been measured for the stress-induced transformation in alloys; the habit plane is not determined by a maximum resolved shear stress condition. The accommodation stresses produced by transformation have very marked effects, and thermal cycling eventually leads to stability of the cubic form down to liquid-air temperatures. LA TRANSFORMATION CUBIQUE-HEXAGONALE DANS LES MONOCRISTAUX DE COBALT ET D'ALLIAGES COBALT-NICKEL Le caractere martensitique de cette modification a et6 confirm6 sur des monocristaux de cobalt et d'alliages de cobalt-nickel par des observations cinetiques et cristallographiques des transformations naturelles et sous tension. La deformation a et& mesuree pour la transformation sous tension dans les alliages; le plan d'habitat n'est pas determine par une tension critique de cisaillement. Les tensions d'accommodation produites par la transformation ont des effets t&s marques et un cycle thermique permet Bventuellement une stabilite de la forme cubique jusqu'a la temperature de l'air liquide. DIE KUBISCH-HEXAGONALE UMWANDLUNG VON EINKRISTALLEN AUS KOBALT UND KOBALT-NICKEL-LEGIERUNGEN. Kinetische und kristallographische Beobachtungen der natiirlichen und der spannungsinduzierten Umwandhmg von Einkristallen aus Kobalt und Kobal&Nickel-Legierungen best&t&ten die martensitische Natur dieser Umwandlung. Bei der spannungsinduzierten Umwandlung von Legierungen wurde die Gestaltsiinderung gemessen, die Habitusebene ist nicht durch eine Bedingung maximaler Schubspannung bestimmt. Die durch die U mwandlung hervorgerufenen Anpassungsspannungen haben sehr ausgepriigte Wirkungen und wiederholtes Gliihen und Abkiihlen fiihrt schliesslich zur Stabilitat der kubischen Modifikation bis hinunter zur Temperatur der fltissigen Luft.