Testing and modelling the influence of irradiation on iodine-induced stress corrosion cracking of Zircaloy-4

✍ Scribed by Isabelle Schuster; Clément Lemaignan; Jacques Joseph

Publisher: Elsevier Science
Year: 1995
Tongue: English
Weight: 567 KB
Volume: 156
Category: Article
ISSN: 0029-5493
DOI: 10.1016/0029-5493(94)00958-2

No coin nor oath required. For personal study only.

📜 SIMILAR VOLUMES

Influence of some factors on the suscept

Influence of some factors on the susceptibility of Zircaloy-2 tubes to iodine stress corrosion cracking

✍ S.W. Sharkawy; F.H. Hammad; A.A. Abou-Zahara; K. Videm 📂 Article 📅 1989 🏛 Elsevier Science 🌐 English ⚖ 702 KB

The effect of axial stress to hoop stres

The effect of axial stress to hoop stress ratio on the susceptibility of unirradiated Zircaloy-4 to iodine stress corrosion cracking

✍ B.C Syrett; R.L Jones; D Cubicciotti 📂 Article 📅 1981 🏛 Elsevier Science 🌐 English ⚖ 1000 KB

Influences of cesium and cesium oxide on

Influences of cesium and cesium oxide on iodine stress corrosion cracking of Zircaloy-2 in out-of-pile and in-pile conditions

✍ Katsumi Une 📂 Article 📅 1979 🏛 Elsevier Science 🌐 English ⚖ 289 KB

The influence of long term use of inhibi

The influence of long term use of inhibitors in hydrochloric acid pickling baths on hydrogen induced stress corrosion cracking

✍ R. Feser; A. Friedrich; F. Scheide 📂 Article 📅 2002 🏛 John Wiley and Sons 🌐 German ⚖ 637 KB

Modelling of reinforcement corrosion – I

Modelling of reinforcement corrosion – Investigations on the influence of shrinkage and creep on the development of concrete cracking in the early propagation stage of reinforcement corrosion

✍ E. Bohner; H.S. Müller 📂 Article 📅 2006 🏛 John Wiley and Sons 🌐 German ⚖ 180 KB 👁 1 views

## Abstract Since the initiation stage of the damage process due to reinforcement corrosion had been successfully investigated in the recent past, the damage progress in the propagation stage is currently in the focus of research. This work deals with the mechanisms of cracking and spalling due to

Report on stress-corrosion cracking of a

Report on stress-corrosion cracking of austenitic chromium-nickel stainless steels. Sponsored by ASTM Committee A-10 on Iron-Chromium, Iron-Chromium-Nickel and related alloys, and NACE unit committee T-5E on stress-corrosion cracking of austenitic stainless steels. ASTM special technical publication No. 264. 92 S., Preis $ 6,–, Mitgl. $ 4,80. 1960, American society for testing and materials, Philadelphia 3

📂 Article 📅 1966 🏛 John Wiley and Sons 🌐 German ⚖ 158 KB