Synthesis of Nanocrystalline Hydroxyapatite Nanorods via Hydrothermal Conditions

✍ Scribed by S. Manafi; M. R. Rahimipour

Publisher
John Wiley and Sons
Year
2011
Tongue
English
Weight
686 KB
Volume
34
Category
Article
ISSN
0930-7516

No coin nor oath required. For personal study only.

✦ Synopsis

The effect of Ca(NO 3 ) 2 •4H 2 O and (NH 4 ) 2 HPO 4 primary solutions as the starting materials in the synthesis of a calcium phosphate phase was examined. Therefore, wet chemical reactions were investigated in solution at different temperatures by hydrothermal conditions aimed at hydroxyapatite (Ca 10 (PO 4 ) 6 (OH) 2 , HAp) synthesis. The powders were investigated by XRD, SEM, FE-TEM, HRTEM, EDAX, SAED, and FTIR. It is found that the HAp have diameters of 25-50 nm and lengths of 120±30 nm with different morphologies. As a matter of fact, the hydrothermal method guarantees the production of HAp for different applications.

📜 SIMILAR VOLUMES

Synthesis and Characterization of Ternar
Synthesis and Characterization of Ternary CuInS2 Nanorods via a Hydrothermal Route
✍ Jianping Xiao; Yi Xie; Rui Tang; Yitai Qian 📂 Article 📅 2001 🏛 Elsevier Science 🌐 English ⚖ 304 KB

Well-de5ned ternary CuInS 2 nanorods 20+25 nm in diameter and 400+450 nm in length were synthesized by the reaction of CuCl 2 , In, CS 2 , and NaOH at temperature as low as 1803C for 15 h when water was used as the solvent. The products were characterized by X-ray di4raction, transmission electron m

Conversion of Calcium Fluorapatiteinto C
Conversion of Calcium Fluorapatiteinto Calcium Hydroxyapatite under Alkaline Hydrothermal Conditions
✍ J.C. Rendón-Angeles; K. Yanagisawa; N. Ishizawa; S. Oishi 📂 Article 📅 2000 🏛 Elsevier Science 🌐 English ⚖ 296 KB

The exchange of F ؊ ions in synthetic calcium 6uorapatite single crystals with OH ؊ was investigated under alkaline hydrothermal conditions. Experiments were performed at various temperatures from 600 to 8003C at 100 MPa, for intervals between 6 and 192 h, in 5 and 10 M KOH solutions. The 6uorapatit

Hydrothermal Synthesis and Characterizat
Hydrothermal Synthesis and Characterization of Nanocrystallineγ-Fe2O3Particles
✍ Dairong Chen; Ruren Xu 📂 Article 📅 1998 🏛 Elsevier Science 🌐 English ⚖ 374 KB

The -Fe 2 O 3 particles with nanometer size have been hydrothermally synthesized using 2-methoxyethanol (MOE)-H 2 O mixed solvent and acetylacetone(Hacac) as additive from iron(II) 2-methoxyethoxides (Fe(MOEO) 2 ). The typical reaction conditions are as follows: reaction temperature 140°C reaction t