Synthesis and properties of radiation modified thermally cured castor oil based polyurethanes

✍ Scribed by Aba Mortley; H.W. Bonin; V.T. Bui

• Publisher: Elsevier Science
• Year: 2007
• Tongue: English
• Weight: 451 KB
• Volume: 265
• Category: Article
• ISSN: 0168-583X
• DOI: 10.1016/j.nimb.2007.08.032

✦ Synopsis

Thermally cured polyurethanes were prepared from castor oil and hexamethylene diisocyanate (HMDI). Due to the long aliphatic chain of the castor oil component of polyurethane, thermal curing of castor oil based polyurethane (COPU) is limited by increasing polymer viscosity. To enhance further crosslinking, COPUs were exposed to doses up to 3.0 MGy produced by the mixed ionizing radiation field of a SLOWPOKE-2 research nuclear reactor. The physico-mechanical properties of castor oil based polyurethanes (COPU), unirradiated and irradiated, were characterized by mechanical tensile tests. A four-fold increase in modulus and tensile strength values from 0.930 to 4.365 MPa and 0.149 to 0.747 MPa, respectively, suggests improved physico-mechanical properties resulting from radiation. The changing areas of the carbonyl and the NH absorbance peaks and the disappearance of the isocyanate peak in the FTIR spectra as radiation progressed, indicates increased hydrogen bonding and intermolecular crosslinking, which is in agreement with the mechanical tests. Unchanging 13 C solid state NMR spectra imply limited sample degradation with increasing radiation.