The subcritical growth of semi-elliptical surface cracks in the front face of a cylindrical disk was calculated. The disk represents a part of a turbine rotor. The stress intensity factors, which are the basis for the calculations presented here, were given in a former paper [l]. The load steps considered consist of an inhomogeneous hoop stress distribution, which occurs at a distinct time-step of the startup procedure of the turbine, and of the stress free state, respectively. By use of a Paris-law the growth of different initial cracks was evaluated under the assumption that the crack geometry remains semi-elliptic.
UnterkriUsches Ri6wachstum von halbelliptischen OberflBchenrissen in einer Twbinenrotorwelle
Das unterkritische Wachstum halbelliptischer Oberflachenrisse in der Stirnseite einer zylindrischen Scheibe wurde berechnet. Die Scheibe ist ein Teil einer Turbinenrotorwelle. Die Spannungsintensitatsfaktoren, die die Grundlage fur die hier vorgestellten Berechnungen bilden, wurden in einer friiheren Arbeit [l] prasentiert. Die untersuchten Lastwechsel bestehen aus einer inhomogenen Umfangsspannungsverteilung, die wahrend eines bestimmten Zeitpunkts des Startvorgangs der Turbine auftritt, sowie dem spannungsfreien Zustand der Rotorwelle. Mittels des Parisgesetzes wurde das Wachstum verschiedener Anfangsrisse ermittelt unter der Voraussetzung, daB die RiDform halbelliptisch bleibt.