Solid solution hardening of gold and other f.c.c. single crystals

✍ Scribed by P. Jax; P. Kratochvil; P. Haasen

• Publisher: Elsevier Science
• Year: 1970
• Weight: 774 KB
• Volume: 18
• Category: Article
• ISSN: 0001-6160
• DOI: 10.1016/0001-6160(70)90029-5

✦ Synopsis

The solid solution hardening rp of Au-In,-Cd,-Ga,-Zn single crystals is measured in the plateau region. A c s/3-dependence fits better than 7) N cl/*. The hardening by different solute atoms in gold is compared with the results on Ag and Cu alloys and with the existing theories. A universal description for all three f.c.c. alloy systems using a combined size and modulus interaction is discussed. DURCISSEMENT DES SOLUTIONS SOLIDES MONOCRISTALLINES D'OR ET D'AUTRES METAUX C.F.C. Le durcissement rp des solutions solides des monocristaux Au-In, Au-Cd, Au-Ga, Au-Zn a 6th mesure dans le domame du plateau. Une loi en c2/s convient mieux que r9 -clle. Le durcissement dG 8. la presence de differents atomes dissous dans l'or est compare aux resultats obtenus pour les alliages a base d'argent et de cuivre, ainsi qu'aux theories existantes. Un modele general pour tous les systemes d'alliages c.f.c. de ces trois metaux, utilisant une interaction combinee de la taille et du module, est discute. MISCHKRISTALLHARTUNG VON GOLD UND ANDEREN KFZ EINKRISTALLEN Messungen der Mischkristallh&rtung r? van Au-In,-Cd,-Ga,-Zn-Einkristallen im Plateaugebiet werden mitgeteilt. Eine cs'r-Abhangigkeit der Plateauspannung r9 padt besser als 7) N cl/r. Die Ergebnisse fur Gold-Einkristalle mit verschiedenen Zusatzen werden mit vorhandenen Messungen an Ag-und Cu-Legierungen verglichen und an Hand der bestehenden Theorien besprochen. Eine einheitliche Beschreibung fur alle 3 k.f.z. Legierungssysteme wird diskutiert, wobei eine kombinierte elastishe Wechselwirkung (Schubmodul-und AtomgrijDendefekt) zwischen Fremdatom und Versetzung angenommen wird.