Plastic-bonded electrodes for nickel—cadmium accumulators: X. The nature of the second discharge step of nickel oxide electrodes

✍ Scribed by B. Klápště; K. Micka; J. Mrha; J. Vondrák

Publisher
Elsevier Science
Year
1982
Tongue
English
Weight
431 KB
Volume
8
Category
Article
ISSN
0378-7753

No coin nor oath required. For personal study only.

✦ Synopsis

The second discharge step of nickel oxide accumulator electrodes is suppressed in the presence of a Teflon binder and/or cobalt, cerium, or manganese hydroxide, whereas the first discharge step increases. This behaviour is discussed in terms of ohmic resistance effects and semiconducting properties of the active material.

📜 SIMILAR VOLUMES

Plastic bonded electrodes for nickel-cad
Plastic bonded electrodes for nickel-cadmium accumulators II. Basic electrochemical parameters of the nickel oxide electrode
✍ J. Mrha; I. Krejčí; Z. Zábranský; V. Koudelka; J. Malík 📂 Article 📅 1979 🏛 Elsevier Science 🌐 English ⚖ 780 KB

Plastic bonded nickel oxide electrodes, prepared at normal temperature by one-stage rolling onto a current collector of steel net or perforated sheet of a mixture of active mass used in pocket-type electrodes, a conducting component and a PTFE binder, were tested in alkaline electrolyte. At current

Plastic-bonded electrodes for nickel—cad
Plastic-bonded electrodes for nickel—cadmium accumulators: VII. Influence of different metal screens on the oxygen recombination rate on plastic-bonded cadmium electrodes
✍ J. Jindra; J. Mrha; M. Musilová; M. Polydorová; J. Peizker 📂 Article 📅 1981 🏛 Elsevier Science 🌐 English ⚖ 431 KB

The oxygen recombination (reduction) rate on plastic-bonded cadmium electrodes in sealed Ni-Cd systems can be increased by using metal screens applied to the gas side of the plastic-bonded cadmium electrode. The metal screen applied should have an optimum geometry (mesh size, wire diameter) to prov

Plastic-bonded electrodes for nickel—cad
Plastic-bonded electrodes for nickel—cadmium accumulators. V. Influence of the current collector and mechanical compression on the current carrying capability of the nickel oxide electrode
✍ V. Koudelka; J. Malík; J. Mrha; I. Krejčí; M. Špinka 📂 Article 📅 1981 🏛 Elsevier Science 🌐 English ⚖ 540 KB

Plastic-bonded nickel oxide electrodes, prepared by rolling a mixture of active material, conductive component and poly(tetrafluoroethylene), were subjected to high rate discharge cycling at 100 mA/cm2 and to an accelerated cycling regime at 20 mA/cm2. The number of cycles, the position of the disch

Electrochemistry of the nickel-oxide ele
Electrochemistry of the nickel-oxide electrode—VII. Potentiostatic step method for study of adsorbed intermediates
✍ B.E. Conway; M.A. Sattar; D. Gilroy 📂 Article 📅 1969 🏛 Elsevier Science 🌐 English ⚖ 842 KB

A method for calculating the charge associated with deposition of adsorbed intermediates at an electrode surface is derived kinetically for the ease of current/time transients arising from a potential step when the steady-state rate of the over-all process is changed as well as the coverage by speci

Evidence for the rate determining step a
Evidence for the rate determining step at the solution—oxide film interface in the anodic growth of thin oxide films at platinum and nickel electrodes in aqueous solutions
✍ A. Damjanovic; L-S.R. Yeh; J.F. Wolf 📂 Article 📅 1981 🏛 Elsevier Science 🌐 English ⚖ 261 KB

The rates of growth of anodic oxide films at PI m acid and alkahna solutions and Ni III alkaline solutibns are compared. In acid solutions, the rates are pH independent. In alkaline solutions. they are affected by pH. The exchange current densities, i,, in alkaline solutions increase one decade as p