Oxygen permeability and structural stability of BaCe0.15Fe0.85O3−δ membranes

✍ Scribed by Xuefeng Zhu; You Cong; Weishen Yang

Publisher
Elsevier Science
Year
2006
Tongue
English
Weight
535 KB
Volume
283
Category
Article
ISSN
0376-7388

No coin nor oath required. For personal study only.

✦ Synopsis

Cobalt-free BaCe x Fe 1-x O 3-δ (x = 0.15-0.85) membranes have both high oxygen permeation flux and high structure stability even in reducing atmosphere at high temperature. The oxygen flux of BaCe 0.15 Fe 0.85 O 3-δ (BCF1585) membrane reached at 0.5 ml/min cm 2 at 900 • C with a thickness of 1.4 mm. Oxygen permeation results showed that oxygen permeation controlling step mainly was oxygen ion diffusion in the membrane bulk if the membrane thicker than 1.0 mm, and mainly was surface oxygen exchange if the membrane thinner than 0.78 mm. Ba 0.5 Sr 0.5 Co 0.8 Fe 0.2 O 3-δ (BSCF) porous layer coated on the membrane surfaces could effectively accelerate the surface oxygen exchange rate, thus greatly improve the oxygen permeability of the membrane. In some cases, the oxygen permeation flux of the membrane coated with BSCF was even two times higher than that of the membrane without coating. Perovskite structure of BCF1585 was still maintained at 950 • C even after it was exposed to 5% H 2 + Ar mixture gas for 1 h.

📜 SIMILAR VOLUMES

Structure and oxygen permeability of Ag-
Structure and oxygen permeability of Ag-doped SrCo0.8Fe0.2O3-δ oxides
✍ Liang Tan; Li Yang; Xuehong Gu; Wanqin Jin; Lixiong Zhang; Nanping Xu 📂 Article 📅 2004 🏛 American Institute of Chemical Engineers 🌐 English ⚖ 125 KB 👁 1 views

## Abstract The powders of SrCo~0.8~Fe~0.2~O~3‐δ~ (SCF) and SCF doped with a different amount of Ag cation are synthesized by a solid‐state reaction method and the corresponding membranes are prepared. XRD results show that the doped Ag promotes the formation of a perovskite structure. The dissolut

Oxygen permeability and stability of Al2
Oxygen permeability and stability of Al2O3-doped SrCo0.8Fe0.2O3−δ mixed conducting oxides
✍ Zhentao Wu; Wanqin Jin; Nanping Xu 📂 Article 📅 2006 🏛 Elsevier Science 🌐 English ⚖ 596 KB

A new series of Al 2 O 3 -doped SrCo 0.8 Fe 0.2 O 3-δ (SCFA) mixed conducting oxides were synthesized by the conventional solid-state reaction method. Effects of doping Al 2 O 3 (1, 3, 5 and 10 wt.%, respectively) on the crystal structure, order-disorder phase transition, microstructure, oxygen perm

Non-monotonic conductivity relaxation of
Non-monotonic conductivity relaxation of proton-conducting BaCe0.85Y0.15O3−δ upon hydration and dehydration
✍ D.-K. Lim; M.-B. Choi; K.-T. Lee; H.-S. Yoon; E.D. Wachsman; S.-J. Song 📂 Article 📅 2011 🏛 Elsevier Science 🌐 English ⚖ 831 KB

The electrical and relaxation properties of Y-doped barium cerate (BaCe 0.85 Y 0.15 O 3Àd ; BCY) were studied as a function of both P O2 and P H2O in the temperature range of 600e900 C. The partial conductivities of protons, holes, and oxygen vacancies were successfully calculated, and the activatio