## Abstract The dynamic tensile modulus and energy loss have been measured for nylon 66 monofilaments at 9 and 60ยฐC. over a wide humidity range in forced longitudinal vibration experiments. The frequency range covered was about 3 to 30 cycles/sec. (radian frequency 20 to 200 sec.^โ1^). The results
## Abstract The presence of spherulites in nylon 66 increases the yield point and reduces the effects of variations in per cent crystallinity. Decreasing the size of the spherulites through increased nucleation results in a higher flexural modulus and yield point, a lower ultimate elongation, and a
To reveal the effect of acid dyes on the melt processing of recycled nylon 66, 17 acid dyes with different chemical structures were used to dye a nylon 66 yarn. The thermal stability of dyestuffs, the thermal degradation of the dyed nylon 66 during compression molding, and the melting and crystalliz