Obscure effect of cathodic polarization on rate of crack propagation during stress corrosion cracking of high-strength steels

✍ Scribed by V. A. Marichev

Publisher
Springer
Year
1975
Tongue
English
Weight
304 KB
Volume
10
Category
Article
ISSN
1573-885X

No coin nor oath required. For personal study only.

πŸ“œ SIMILAR VOLUMES

An ambiguity of the cathodic polarizatio
An ambiguity of the cathodic polarization effect on crack growth during stress corrosion cracking of aluminum alloys
✍ V. A. Marichev πŸ“‚ Article πŸ“… 1983 πŸ› John Wiley and Sons 🌐 German βš– 652 KB

## Abstract The kinetics of crack growth under the conditions of stress corrosion cracking of aluminum alloys in electrolytes with different anion composition and pH values from 0 to 13 has been studied. It is shown that for the majority of alloy‐electrolyte systems anodic polarization accelerates

Mechanism of corrosion fatigue crack pro
Mechanism of corrosion fatigue crack propagation in high strength steels
✍ Nakasa Keijiro; Takei Hideo; Itoh Hisashi πŸ“‚ Article πŸ“… 1983 πŸ› Elsevier Science 🌐 English βš– 922 KB

The crack propagation velocity in corroGon fatigue (du/dN), were measured on the Ni-Cr-Mo steel quenched and tempered at 473 or 773 K. The steel with high sensitivity to delayed failure reveals the largest (du/dN), under square load and the smaller (da/dN), under positive saw tooth load. The frequen