Morphology and growth mechanism of aligned ZnO nanorods grown by catalyst-free MOCVD

โœ Scribed by M. Rosina; P. Ferret; P.-H. Jouneau; I.-C. Robin; F. Levy; G. Feuillet; M. Lafossas

Publisher
Elsevier Science
Year
2009
Tongue
English
Weight
663 KB
Volume
40
Category
Article
ISSN
0026-2692

No coin nor oath required. For personal study only.

๐Ÿ“œ SIMILAR VOLUMES

Catalyst-free synthesis and luminescence
Catalyst-free synthesis and luminescence of aligned ZnO nanorods
โœ Aurangzeb Khan; Wojciech. M. Jadwisienczak; Henryk. J. Lozykowski; Martin E. Kor ๐Ÿ“‚ Article ๐Ÿ“… 2007 ๐Ÿ› Elsevier Science ๐ŸŒ English โš– 626 KB

Quasi-aligned undoped ZnO nanorods with diameter in the range 100-300 nm and length of several micrometers have been grown catalyst-free on Si(1 0 0) wafer in a one-step process by direct heating of Zn powders. All nanowires are single crystals and are aligned vertically to the substrate surface wit

Low-Temperature Growth of Well-Aligned Z
Low-Temperature Growth of Well-Aligned ZnO Nanorods by Chemical Vapor Deposition
โœ J.-J. Wu; S.-C. Liu ๐Ÿ“‚ Article ๐Ÿ“… 2002 ๐Ÿ› John Wiley and Sons ๐ŸŒ English โš– 251 KB ๐Ÿ‘ 2 views

electroluminescent conjugated polymers. As an example, Figure 3 shows the anisotropic optical constants of a film of F8BT. The ordinary absorption was again in good agreement with the spectrum obtained from normal incidence transmission measurements. Although not as anisotropic as OC1C10ยฑ PPV, F8BT