Measurement of surface tension of tantalum by a dynamic technique in a microgravity environment

✍ Scribed by A. P. Miiller; A. Cezairliyan

• Publisher: Springer
• Year: 1993
• Tongue: English
• Weight: 654 KB
• Volume: 14
• Category: Article
• ISSN: 0195-928X
• DOI: 10.1007/bf00505676

✦ Synopsis

A dynamic technique has been used in a microgravity environment to measure the surface tension of tantalum at its melting point. The basic method involves resistively heating a tubular specimen from ambient temperature to temperatures above its melting point in about 1 s by passing an electrical current pulse through it, while simultaneously measuring the pertinent experimental quantities with millisecond resolution. A balance between the magnetic and the surface tension forces acting on the specimen is achieved by splitting the current after it passes through the specimen tube and returning a fraction of the current along the tube axis and the remaining fraction concentrically outside the specimen. Values for surface tension are determined from measurements of the equilibrium dimensions of the molten specimen tube and the magnitudes of the currents. Rapid melting experiments were performed during microgravity simulations with NASA's KC-135 aircraft and the results were analyzed, yielding a value of 2.07 4-0.06 N. m-t for the surface tension of tantalum at its melting point. Conditions for improving specimen stability during temperature excursions into the liquid phase are discussed.