The surf8ce diffusion coefficient of copper at 906ยฐC is evaluated utilizing a new technique involving the coalescence of two gas-filled bubbles in the interior of the metal. The value obtained is in good agreement with measurements by other techniques, and demonstrates the feasibility of this method for obtaining surface diffusion values under very clean surface conditions. The method is also 8ppliC8ble to the case of spherical precipitate particles and thus offers 8 means of assessing interfsciel diffusivities, felt to be of great importance in many solid-state transformations.
MESURE DES COEFFICIENTS
; DEj DIFFUSION EN SURFACE PAR LA COALESCENCE DE BULLES DE:GAZ RARES L'auteur a 6value le coefficient de diffusion en surface du cuivre 8. 900ยฐC 8 l'aide d'une nouvelle technique faisant intervenir la coalescence de deux bulles contenant du gaz 8 l'int&ieur du metal. La valeur ainsi obtenue est en bon accord avec les mesures realisees par d'autres techniques, montr8nt ainsi la possibilite d'obtenir les coefficients de diffusion en surface lorsque la surface de l'echantillon eat t&s propre. Cette methode eat Bgalement applicable dans le oas de precipites spheriques et offre le moyen d'etablir des diffusivites interfaciales qui sont d'uno grande import8nce dans plusieurs transformations 8 1'6tat solide. MESSUNG VON KOEFFIZIENTEN DER OBERFLACHENDIFFUSION DURCH ,KOALESZENS INERTER GASBLASEN Der Oberfliichendiffusionskoeffizient von Kupfer bei 900ยฐC ist mit einer neuen Technik, der Komleszens zweier gesgeftillter Blilschen im Intern des Metalls, bestimmt worden. Das Ergebnis ist in guter Ubereinstimmung mit anderen MeSmethoden Es zeigt, daD dieses Verfahren zur Bestimmung von Werten der Oberfl~hendiffusion unter sehr reinen Oberfliichenbedingungen geeignet ist. Die Methode kann such auf spharische Ausscheidungsteilchen angewandt werden und gest8ttet daher, Grenzflachendiffusion zu untersuchen, w&s fur viele Umwandlungen im festen Zustand von groger Wichtigkeit ist.