The mechanical properties of a solution treated and double aged nickel -18% iron -18% chromium alloy (Inconel 718) were studied to assess its utility at temperatures in the ambient-to-cryogenic range. Uniaxial tensile property measurements using unnotched specimens at decreasing temperatures between 295 and 4 K show that yield and ultimate strengths increase by 20% and 29%, respectively, while ductility remains virtually constant. Fracture mechanics tests using 2.54 cm thick compact specimens revealed that the fatigue crack growth resistance of this alloy improves slightly at extreme cryogenic temperatures, and its plane strain fracture toughness, El c, increases from 96.3 MPa m '/" at 295 K to 112.3 MPa m ~ at 4 K. These results are compared with similar data for Inconel 750 alloys
π SIMILAR VOLUMES
## Abstract The hot corrosion behaviour of a platinum containing nickel based superalloy (RJM 2012) is compared with that of a similar alloy (IN 792 + Hf) without platinum. The results of burner rig testing at 800Β°C showed that the oxide scales on the platinum containing alloy were still very prote
## Abstract The effect of crystal orientation on the microstructure of a nickelβbased crystalline superalloys during directional solidification was explored. Differently oriented crystals with [001] and [011] orientations were fabricated with seeding technique. The results showed that primary dendr
## Abstract Various modifications of the eutectic, directionally solidified superalloy 73 C were investigated with respect to creep fatigue effects. This was carried out using a thermal cycling apparatus where a mechanical uniaxial load could be applied. A high volume fraction of carbides had an im
## Abstract The ageing behaviour of trimethylolpropane trioleate was investigated at different temperatures in a modified rotary bomb test apparatus. Some physicochemical properties of ageing oil samples, such as acid value, kinematic viscosity, and iodine value, were measured. The oil samples were