Investigation and modeling of the kinetics of the development of corrosion-fatigue cracks

✍ Scribed by N. N. Vasserman; V. A. Merkushev; M. S. Nemanov

Publisher: Springer
Year: 1978
Tongue: English
Weight: 435 KB
Volume: 13
Category: Article
ISSN: 1573-885X
DOI: 10.1007/bf00716111

No coin nor oath required. For personal study only.

📜 SIMILAR VOLUMES

Development of corrosion-fatigue cracks

Development of corrosion-fatigue cracks from the fracture of samples

✍ G. T. Nazarenko; I. I. Ishchenko 📂 Article 📅 1978 🏛 Springer US 🌐 English ⚖ 751 KB

Some problems in investigating the devel

Some problems in investigating the development of fatigue cracks

✍ A. Z. Vorob'ev 📂 Article 📅 1980 🏛 Springer 🌐 English ⚖ 549 KB

Development of corrosion fatigue cracks

Development of corrosion fatigue cracks in ship hull aluminum alloys

✍ A. P. Olik; L. N. Petrov; A. V. Bakulin; A. Yu. Kalinkov 📂 Article 📅 1988 🏛 Springer 🌐 English ⚖ 261 KB

Development of corrosion-fatigue cracks

Development of corrosion-fatigue cracks in round cross section samples

✍ G. T. Nazarenko; I. I. Ishchenko 📂 Article 📅 1982 🏛 Springer 🌐 English ⚖ 733 KB

Methods of investigating the corrosion-f

Methods of investigating the corrosion-fatigue strength and stress-corrosion cracking of materials at high temperatures and pressures

✍ I. Yu. Liskevich; N. N. Tkachenko; B. F. Koliushko; R. K. Melekhov; I. I. Vasile 📂 Article 📅 1972 🏛 Springer 🌐 English ⚖ 200 KB

The significance of stress corrosion cra

The significance of stress corrosion cracking in corrosion fatigue crack growth studies

✍ D. Rhodes; J.K. Musuva; J.C. Radon 📂 Article 📅 1981 🏛 Elsevier Science 🌐 English ⚖ 1005 KB

Abslraet-A model is proposed to account for interactions between fatigue and stress corrosion crack propagation mechanisms in appropriate corrosion fatigue conditions. Tests on an alloy steel, and both wrought and cast aluminium alloys, are reported. Despite the use of very simple coefficients in th