Development of corrosion-fatigue cracks from the fracture of samples

โœ Scribed by G. T. Nazarenko; I. I. Ishchenko

Publisher
Springer US
Year
1978
Tongue
English
Weight
751 KB
Volume
14
Category
Article
ISSN
1573-8582

No coin nor oath required. For personal study only.

๐Ÿ“œ SIMILAR VOLUMES

The significance of stress corrosion cra
The significance of stress corrosion cracking in corrosion fatigue crack growth studies
โœ D. Rhodes; J.K. Musuva; J.C. Radon ๐Ÿ“‚ Article ๐Ÿ“… 1981 ๐Ÿ› Elsevier Science ๐ŸŒ English โš– 1005 KB

Abslraet-A model is proposed to account for interactions between fatigue and stress corrosion crack propagation mechanisms in appropriate corrosion fatigue conditions. Tests on an alloy steel, and both wrought and cast aluminium alloys, are reported. Despite the use of very simple coefficients in th

A fracture model of corrosion fatigue cr
A fracture model of corrosion fatigue crack propagation of aluminum alloys based on the material elements fracture ahead of a crack tip
โœ Rong Wang ๐Ÿ“‚ Article ๐Ÿ“… 2008 ๐Ÿ› Elsevier Science ๐ŸŒ English โš– 919 KB

In this study, attempts were made to extend the concept of material elements fracture ahead of a crack tip during fatigue crack propagation (FCP) to corrosion fatigue crack propagation (CFCP) of aluminum alloys in a corrosive environment. Considering the effect of corrosion damage on the material el