Internal friction in oxygen-vanadium and nitrogen-vanadium solid solutions

✍ Scribed by R.W Powers

• Publisher: Elsevier Science
• Year: 1954
• Weight: 449 KB
• Volume: 2
• Category: Article
• ISSN: 0001-6160
• DOI: 10.1016/0001-6160(54)90195-9

✦ Synopsis

Two internal friction peaks have been identified in vanadium. One occurring at 186°C for frequencies of 1 cps is associated with the stress-induced diffusion of oxygen, and the other occurring at 272°C is associated with the diffusion of nitrogen. The corresponding activation energies for these peaks were found to be 28.6 and 34.1 kcal, respectively. The skewness of the oxygen pe& has been shown to be a concentration effect. LE FROTTEMENT INTERNE DANS LES SOLUTIONS SOLIDES OXYGfiNE-VANADIUM ET AZOTE-VANADIUM Deux maxima de frottement interne furent trouves dans le vanadium. Un de ces maxima a lieu B 186°C pour des frequences d'un cycle par seconde; il est dQ a la diffusion de l'oxygene, induite par des tensions. L'autre a lieu a 272°C et est d6 B la diffusion de l'azote. Les ener ies d'activation correspondantes & ces maxima furent &ah&s B 28,6 et 34,l Kcal respectivement. % n I'asymetrie du maximum associe & I'oxygene est un effet de concentration. a montre que INNERE REIBUNG IN DEN FESTEN LUSUNGEN VANADIUM-SAUERSTO~~ UND VANADIUM-STICKSTOFF Zwei Maxima der inneren Reibung wurden in Vanadium identifiziert. Das eine Maximum tritt bei 186'C und Frequenzen von einem Hz auf und hangt mit der spannungsinduzierten Diffusion des Sauerstoffs zusammen. Das zweite Maximum, das bei 272'C auftritt, steht mit der Diffusion des Stickstoffs in Zusammenhang. Die zu diesen Maxima gehorenden Aktivierungsenergien betrugen 28,6 Kcal und 34,l Kcal. Es wurde gezeigt, dass die schiefe Form des Sauerstoffmaximas auf einem Konzentrationeffekt beruht.