Two "abnormal" peaks, occurring in the temperature ranges 116-166°C and 221-242% at 1 C/S, and having activation energies of 25 and 31 kcal/ mole, respectively, were found by nitriding with ammonia at 690°C specimens of dilute Fe-Ti alloys (0.15 to 0.60 wfo Ti). Peak temperatures and widths varied with oomposition and heat treatment. Both peaks were suppressed by heating at about 97O"C, and are considered to be due to interstitial nitrogen-titanium interaction. FROTTEMENT INTERNE DANS LES ALLIAGES Fe-Ti-N Deux pits nouveaux, se produisant entre 116 et 166°C et 221 et 242°C a 1 c/s, et ayant des Energies d'sctivation respectivement &gales S 26 et 31 kcal/ mole, ont 6% mis en Evidence en nitrurant des eehantillons d'alliage Fe-Ti d&.&s (0,15 8, O,SO% Ti en poids) avec de I'ammoniac a 590% Les temparatures et les largeurs des pies varient avec la composition et le traitement thermique. Les deux pies disparaissent par chauffage a 970°C environ, et l'auteur oonsid&e qu'ils sont d& $, l'interaction interstitiel d'azotetitane. INNERE REIBUNG IN Fe-Ti-N-LEGIERUNGEN Nach Nitrierung dtiiissiger Fe-Ti-Legisrungen (0,16 bis 0,60 Gew. y0 Ti) mit Ammoniak bei 590°C wurden zwei "anomale" Maxima in den Tern eraturbereichen 116-166'C und 221-242°C bei 1 Kz mit Aktivierungsenergien von 25 bzw. 31 kcal Mol gefunden. Die Temperatur und Breite der iMaxima &ndert sich mit der Zu~~en~tzun~ und bei II ~ebehandl~g. Beide Maxima verschwanden nach Aufwarmen auf &we 970°C; es wird angenommen, da6 sie von der Weoh~lwirkung swisohen Stick&off-Zwischengitteratomen und Tit.anatomen herriihren.
📜 SIMILAR VOLUMES
Experimental data on the dist~bution of aluminum between liquid iron and silver at 1600°C are presented. The effects of carbon and silicon in the iron are shown. Recent data of Hillert on the cell: Al(s) /AlClr in NaCI(l) [AI-Ag alloy(s) are extrapolated to obtain the activity of aluminum in liquid