Improving the ductility of intermetallic compounds by particle-induced slip homogenization

โœ Scribed by Ian Baker

Book ID
114388817
Publisher
Elsevier Science
Year
1999
Tongue
English
Weight
92 KB
Volume
41
Category
Article
ISSN
1359-6462

No coin nor oath required. For personal study only.

๐Ÿ“œ SIMILAR VOLUMES

Determination of slip systems and their
Determination of slip systems and their relation to the high ductility and fracture toughness of the B2 DyCu intermetallic compound
โœ G.H. Cao; D. Shechtman; D.M. Wu; A.T. Becker; L.S. Chumbley; T.A. Lograsso; A.M. ๐Ÿ“‚ Article ๐Ÿ“… 2007 ๐Ÿ› Elsevier Science ๐ŸŒ English โš– 579 KB

DyCu single crystals with CsCl-type B2 structure were tensile tested at room temperature. Slip trace analysis shows that the primary slip system in DyCu with a tensile axis orientation of AE1 1 0ae is {1 1 0}AE0 0 1ae and the critical resolved shear stress for {1 1 0}AE0 0 1ae slip is 18 MPa. Slip t

The Mobility of Grown-in Dislocations in
The Mobility of Grown-in Dislocations in the Intermetallic Compound MgZn2. III. Dependence of Basal Slip on Chemical Composition within the Homogeneity Range and on Temperature
โœ H. Kubsch; P. Paufler; G. E. R. Schulze ๐Ÿ“‚ Article ๐Ÿ“… 1973 ๐Ÿ› John Wiley and Sons ๐ŸŒ English โš– 196 KB

## Abstract The dislocation velocity, , in basal slip shows a maximum within the range of homogeneity of the Laves phase MgZn^2^. The temperature dependence of can be described by an thermally activated mechanism with an activation enthalpy of (1.7 ยฑ 0.3) eV in agreement with macroscopic deformati