Electrical resistivity observations on quenched and cold-worked magnesium

✍ Scribed by C.J Beevers

• Book ID: 102979937
• Publisher: Elsevier Science
• Year: 1963
• Weight: 693 KB
• Volume: 11
• Category: Article
• ISSN: 0001-6160
• DOI: 10.1016/0001-6160(63)90190-1

✦ Synopsis

Electrical resistivity measurements on quenched and cold-worked magnesium have been carried out.

From the quenching experiments it was found that the formation energy of vacancies in magnesinm is 0.89 $7 0.06 eV. Tbe annealing behaviour of cold-worked magnesium is complex, but it is concluded that in the temperature range 0°C to 50% vacancies are mobile and migrate with an a&iv&ion energy of approxima~ly 0.5 0V.

MESURES

DE RESISTIVITE ELECTRIQUE SUR LE MAGNESIUM TREMPE ET DEFORME A FROID L'aut8eur a effectue des mesures de resistivit6 electrique SUP du magnesium trempe et deform8 ii froid. Les esseis de trempe oat permis de determiner I'energie de formation de lacunes drtns IQ msgnesium: 0,89 $--0,06 eV. Le comportement au recuit du magnesium d&fox-me & froid est complexe, mais on peut conclure que, dans le domaine de temperatures de 0 I 5O"C, Ies lacunes sont mobiles et diffusent nveo une hnergie d'activation d'environ 0,5 eV. BEOBACHTUNGEN DES ELEKTRISCHEN WIDERSTANDES AN ABGESCHRECKTEM UND KALTVERFORMTEM MAGNESIUM An abgeschrecktem und kaltverformtem Magnesium wurden Messungen des elektrischen Widerstandes durchgefiihrt. Aus den Abschreckversuchen ergab sich die Bildungsenergie von Leer&e&n in Magnesium zn 0.89 & 0.06 eV. Das Erholungsverhalten von kaltverformtem Magnesium ist komplex, aber es wird gesoblossen, daIj im Temperaturbereich 0°C bis 50°C Leerstellen beweglich sind und mit einer Aktivierungsenergio von etwa 0.5 eV wandern.