Effect of exposure conditions on the oxidation of MCrAlY-bondcoats and lifetime of thermal barrier coatings

✍ Scribed by M. Subanovic; P. Song; E. Wessel; R. Vassen; D. Naumenko; L. Singheiser; W.J. Quadakkers

Publisher
Elsevier Science
Year
2009
Tongue
English
Weight
788 KB
Volume
204
Category
Article
ISSN
0257-8972

No coin nor oath required. For personal study only.

📜 SIMILAR VOLUMES

Effect of manufacturing related paramete
Effect of manufacturing related parameters on oxidation properties of MCrAlY-bondcoats
✍ M. Subanovic; D. Sebold; R. Vassen; E. Wessel; D. Naumenko; L. Singheiser; W. J. 📂 Article 📅 2008 🏛 John Wiley and Sons 🌐 German ⚖ 569 KB

## Abstract The effect of MCrAlY‐bondcoat manufacturing parameters prior to TBC deposition on the bondcoat oxidation behavior and TBC lifetime was studied. The studied material was a NiCoCrAl(Y/Hf) free‐standing coating. It was found that variation of oxygen partial pressure during vacuum plasma sp

Effect of atmosphere composition on the
Effect of atmosphere composition on the oxidation behavior of MCrAlY coatings
✍ P. Song; M. Subanovic; J. Toscano; D. Naumenko; W. J. Quadakkers 📂 Article 📅 2010 🏛 John Wiley and Sons 🌐 German ⚖ 558 KB

## Abstract In the present work the effect of atmosphere composition on the growth rate and adherence of the alumina scales was studied using free‐standing MCrAlY‐coatings and TBC‐specimens with MCrAlY‐bondcoats. The exposures comprised isothermal and cyclic exposures in laboratory air and Ar‐H~2~‐

Effect of ion implantation on growth of
Effect of ion implantation on growth of thermally grown oxide in MCrAlY coating for TBC
✍ Eungsun Byon; Shihong Zhang; Sung-Hun Lee; Goo-Hyun Lee; Sik-Chol Kwon 📂 Article 📅 2010 🏛 Elsevier Science 🌐 English ⚖ 757 KB

Thermal barrier coatings (TBCs) have been widely used in various gas turbines for aircraft propulsion and power generation. TBCs consist of a metal bond coat and a ceramic top coat of YSZ. It is generally known that the TBC′ life strongly depends on the thermally grown oxide (TGO) because failure of