Section of Metallurgy and Material Engineering of the Mining Academy,
Freiborg/Sachsen
Dislocation Densities in Copper Single Crystals after Thermal Treatment l )
Copper crystals of high purity and doped with nickel were subjected t o a long time thermal treatment a t 1050 "C, in order to reduce the as-grown dislocation density of about lo7 cm+. A dissolution of the dislocations during their motion to the crystal surface was observed. Regions of different dislocation densities &Pose. Finally the crystals exhibited constant dislocation densities of lo2 cm-2. Such a perfection or a better one of the crystals is reached only by a long time treatment, since the dislocation velocity without external stresses cannot exceed 1 . 10-7 cms-1 in copper single crystals of high purity.
Reinste sowie nickeldotierte Kupfereinkristalle wurden, um die eingewachsene Versetzungsdichte von etwa 107 cm-2 herabzusetzen, einer langdauernden Warmebehandlung bei 1050 "C unterworfen. Es wurde eine Auflosung der Versetzungen wahrend ihrer Bewegung zur Kristalloberfliiche beobachtet. Es entstanden Zonen unterschiedlicher Versetzungsdichte. Die Kristalle hatten schlieDlich konstante Versetzungsdichten von 102 om-2 aufzuweisen. Eine derartige oder bessere Perfektion der Kristalle wird nur durch eine liingere Gliihdauer erreicht, da die Versetzungsgeschwindigkeit ohne 6uBere Spannung in reinsten Kupferkristallen nicht gro13er als etwa 1 .
cm . s-l werden kann.