Dilation of h.c.p. zirconium by interstitial deuterium

✍ Scribed by S.R MacEwen; C.E Coleman; C.E Ells; J Faber jr

• Publisher: Elsevier Science
• Year: 1985
• Weight: 502 KB
• Volume: 33
• Category: Article
• ISSN: 0001-6160
• DOI: 10.1016/0001-6160(85)90098-7

✦ Synopsis

Time-of-flight neutron diffraction has been used to measure the dilation of h.c.p. Zr by interstitial deuterium at 727 and 777 K. The dilation per atom of D is 2.78 A3, and the partial molal volume is 1.67 cm3/mol. The lattice strain in the (c)-direction is 1.65 times greater than in the (a)-direction, and assuming tetragonal symmetry, the components of the I-tensor are found to be 1, = 0.032 and 1, = 0.052.

Rbum~Nous

avons utilisi la diffraction de neutrons avec temps de vol pour mesurer la dilatation du Zr hc provoqute par l'insertion de deuttrium g 727 et 777 K. La dilatation par atome de D est tgale B 2.78 Al et le volume molaire partiel est &gal $ 1,67 c&/mole. La d&formation du r&au dans la direction (c) est 1,65 fois plus grande que dans la direction (a) et, si l'on admet que l'on a une symetrie quadratique, les composantes du tenseur 1 sont I, = 0,032 et 1, = 0,052. Zusammenfassung-Die Aufweitung des hexagonal dichtest gepackten Zirkons durch interstitielles Deuterium wurde mittels Flugzeit-Neutronenbeugung bei 727 und 777 K gemessen. Die Auweitung betrlgt 2,78 A3 pro Deuteriumatom, das partielle molare Volumen ist I,67 cm'/Mol. Die Gitterdehnung ist in der (c)-Richtung 1,65-ma1 grinder als in der (a)-Richtung. Mit der Annahme tetragonaler Symmetrie ergeben sich die Komponenten des I-Tensors zu 1,-0,032 und I, = 0,052.