Diffusion Cells and Chemical Failure of MCrAlY Bond Coats in Thermal-Barrier Coating Systems

✍ Scribed by H. E. Evans; M. P. Taylor

Book ID
110290668
Publisher
Springer-Verlag
Year
2001
Tongue
English
Weight
560 KB
Volume
55
Category
Article
ISSN
0030-770X

No coin nor oath required. For personal study only.

πŸ“œ SIMILAR VOLUMES

Spalling failure of a thermal barrier co
Spalling failure of a thermal barrier coating associated with aluminum depletion in the bond-coat
✍ E.A.G Shillington; D.R Clarke πŸ“‚ Article πŸ“… 1999 πŸ› Elsevier Science 🌐 English βš– 800 KB

AbstractÐA plasma-sprayed thermal barrier coating is observed to spall after oxidation at 11218C from a CoNiCrAlY bond-coated superalloy at the interface between the thermally grown oxide (TGO) and the zirconia thermal barrier coating (TBC). Phase characterization by photostimulated luminescence and

The influence of bond coat surface rough
The influence of bond coat surface roughness on chemical failure and delamination in TBC systems
✍ M. P. Taylor; W. M. Pragnell; H. E. Evans πŸ“‚ Article πŸ“… 2008 πŸ› John Wiley and Sons 🌐 German βš– 340 KB

## Abstract Localised loss of aluminium from the bond coat within thermal barrier coating (TBC) systems is a critical factor determining the lifetime of these coatings. In this paper, it will be demonstrated that electroplated MCrAlY bond coats with asperities of high aspect ratios can experience p