The diffusion coefficient of oxygen has been measured in niobium, vanadium and several dilute substitutional niobium alloys. Measurements were made over the range of 6@I-1150Β°C (873-1423 K) using a solid electrolytic cell technique. Oxygen diffusivity in the alloys was found to be less than in pure niobium. This is interpreted as being due to trapping of oxygen atoms by the substitutional solute atoms. The estimated substitutional-oxygen binding or 'trap' energies (in eV) for the solutes investigated are: Ta, 0.3 + 0.1: V, 0.55 + 0.05; Ti, 0.7 f 0.1; Zr, 0.7 f 0.05.
Rksumk-Nous
avons mesure le coefficient de diffusion de l'oxygene dans le niobium. le vanadium et quelques alliages substitutionnels dilub de niobium. Nous avons effectut des mesures entre 600 et 1150Β°C (8731423 K), par la technique de la cellule ii electrolyte solide. Nous avons trouve que la diffusivite de l'oxygene dans les alliages Ctait inferieure 1 la dilTu.sivitC de l'oxygene dans le niobium pur. Nous interprettons cette observation par un piegeage des atomes d'oxygine par les atomes du solute en substitution. L'e-stimation des energies (en eV) de liaison (ou de "piegeage") entre un atome substitutionnel et un atome d'oxygtne donne les valeurs: Ta, 0,3 + 0.1; V, 0,55 & 0,05; Ti, 0,7 + 0.1; Zr. 0.7 f 0.05. ZusammenfassuneDer Diffusionskoefhzient von Sauerstoff wurde in Niob, Vanadium und verschiedenen verdllnnten;ubstitutionellen Nioblegierungen gemessen. Diese Messungen wurden mittels einer Technik mit fester elektrolvtischer Zelle tlber den Temneraturbereich 600-l 150Β°C (8731423 K) durchgefdhrt. In den Legierungen war die Sauerstoffdiffusidn geringer als in reinem Niob. Dieser Befund wird dem Einfangen von Sauerstoffatomen an substitutionell gel&ten Atomen zugeschrieben. Die daraus abgeschatxten Bindungsenergien zwischen Sauerstoff und geliistem Atom sind (in eV): Ta, 0,3 + 0.1; V. 0.55 + 0,05; Ti, 0.7 + 0.1; Zr, 47 & 405.