Silver-doped rocksalt crystals were treated with different hydrocarbons and with a mixture of CH, and 0% at higher temperatures. Besides decoration of dislocations and in some oases cavity formation, spiral etch-pits were formed after a treatment with CH, and 0,. The decoration is due to electrons from hydrogen or free radicals. The spiral etch-pits are presumably formed by an inhomogeneous concentration of reaction products in the gaseous vapour phase round an active site.
LA DECORATION ET L'ATTAQUE DE CRISTAUX DE SEL GEMME DOPES
A L'ARGENT AU COURS DE REACTIONS SUPERFICIELLES GAZEUSES Les auteurs ant trait6 des cristaux de se1 gemme dopb & l'argent par different hydroearbures et par un melange de CH, et d'0, a des temperatures plus &levees. A c&e de la decoration des dislocations et dans certains cas de la formation de oavites, des piqdres de corrosion en spirale ont et6 obtenues apres un traitement au CH, et a1'0,. La d&oration est due aux electrons de l'hydrogene ou des radicaux libres. Les piqiires de corrosion en spiral8 sont vraisembl&blement form&s par une concentration non homogene de produits de la reaction dans la phase gazeuse et Za proximit& dun site a&if. DEKORIERUNG UND ATZUNG VON SILBERDOTIERTEN STEINSALZKRISTALLEN DURCH GASREAKTIONEN AN DER OBERFLACHE Silberdotierte Steinsalzkristalle wurde mit verschiedenen Kohlenwasserstoffen und mit einer Mischung von CH, und Oe bei hiiheren Temper&mm behandelt. Ausser der Dekorierung von Versetzungen und gelegentlioher Bildung von Hohlraumen entstanden nach einer Behandlung mit CH, und 0, spiralartige Pitzgrtibchen. Die Dekorierung riihrt von Elektronen von Wasserstoff oder freien Radikalen her. Die spiralfijrmigen Atzgriibohen bilden sich vermutlioh infolge einer inbomogenen Konzentration der Reaktionsprodukte in der gasfijrmigen Dampfphase in unmittelbarer Umgebung einer aktiven Stelle.