Critical current density of filamentary NSG123 superconductors in high magnetic field

✍ Scribed by Y. Ikebe; E. Ban; Y. Matsuoka; G. Nishijima; K. Watanabe

Publisher
Elsevier Science
Year
2007
Tongue
English
Weight
454 KB
Volume
463-465
Category
Article
ISSN
0921-4534

No coin nor oath required. For personal study only.

✦ Synopsis

Nd 0.33 Sm 0.33 Gd 0.33 ) 1.18 Ba 2.12 Cu 3.09 O y filaments have been successfully fabricated by a solution spinning method and OCMG processing. We have systematically investigated the relationship between cooling rate from the partial-melting temperature and transport J c value for filamentary samples treated in 0.1%O 2 + Ar. It was found that both the J c value and the microstructure of samples depended on the cooling rate. The samples partially melted at 1050Β°C and cooling rate of 10-50 Β°C/h showed J c value higher than 10 4 A/cm 2 . The maximum J c value of 3.0 β€’ 10 4 A/cm 2 was obtained for 40 Β°C/h sample. The transport J c was also measured at 83-90 K in external magnetic fields up to 17 T. The 10 Β°C/h sample exhibited superior J c behavior and a J c value of 1.1 β€’ 10 3 A/cm 2 at 83 K was maintained up to 17 T, in which fine (Nd,Sm,Gd) 2 BaCuO 5 particles about 1 lm in diameter were homogeneously dispersed.

πŸ“œ SIMILAR VOLUMES

Initial composition dependence of the cr
Initial composition dependence of the critical current density in filamentary NSG123 superconductors
✍ Y. Ikebe; E. Ban; Y. Matsuoka; G. Nishijima; K. Watanabe πŸ“‚ Article πŸ“… 2008 πŸ› Elsevier Science 🌐 English βš– 187 KB

The effect of the starting composition on the superconducting properties for ternary system (Nd, Sm, Gd)-Ba-Cu-O filaments was systematically investigated. The filaments with the composition of (Nd 0.33 ,Sm 0.33 ,Gd 0.33 ) 1.18 Ba 2.12 Cu 3.09 O y (sample A), (Nd 0.50 ,Sm 0.25 ,Gd 0.25 ) 1.18 Ba 2.1

Enhancement of critical current density
Enhancement of critical current density in Gd123 bulk superconductor doped with magnetic powder
✍ Y. Xu; M. Izumi; Y.F. Zhang; Y. Kimura πŸ“‚ Article πŸ“… 2009 πŸ› Elsevier Science 🌐 English βš– 318 KB

We studied the materials processing to grow high performance magnet with doping of magnetic powder as candidature of pinning centers. The magnetic powder was doped into Gd123 matrix and grew into single domain bulk in air. With doping magnetic powder in Gd123 bulk superconductors, the flux pinning w

On the magnetic field dependence of crit
On the magnetic field dependence of critical current density in single crystals of high-Tc superconductors
✍ K. Yamafuji; T. Fujiyoshi; K. Toko; T. Matsuno; T. Kobayashi; K. Kishio πŸ“‚ Article πŸ“… 1994 πŸ› Elsevier Science 🌐 English βš– 849 KB

The critical current density, J,, is discussed theoretically to explain the exponential dependence of .I, on the flux density, B, given typically by J,rexp( -B/B,( T) ), which has been widely observed for single crystals of high-T, superconductors in an external magnetic field parallel to the crysta

Magnetic field dependence of the critica
Magnetic field dependence of the critical currents in high Tc superconductors
✍ Ljiljana DobrosavljeviΔ‡-GrujiΔ‡; Zoran RadoviΔ‡ πŸ“‚ Article πŸ“… 1991 πŸ› Elsevier Science 🌐 English βš– 188 KB

It is shown, within a simple model calculation, that the critical current density of an S/N/S junction in a high paralel magnetic field decays exponentially. The comparison of the theoretical results with experimental data for the Pb/Cd/Pb junction and YBCO films is given.