Comparative crack layer analysis of fatigue and creep crack propagation in high density polyethylene

✍ Scribed by M.L. Kasakevich; A. Moet; A. Chudnovsky

Publisher
Elsevier Science
Year
1990
Tongue
English
Weight
554 KB
Volume
31
Category
Article
ISSN
0032-3861

No coin nor oath required. For personal study only.

πŸ“œ SIMILAR VOLUMES

A study of crack propagation in high-den
A study of crack propagation in high-density polyethylene
✍ Ray D. Hoffman πŸ“‚ Article πŸ“… 1982 πŸ› John Wiley and Sons 🌐 English βš– 869 KB

In recent published work a method was proposed to calculate fracture toughness during the crack-propagation phase of the loading of notched specimens. In this paper, it is proposed that the fracture toughness J can have a value that does not exceed the product of the ultimate work to failure of the

Effect of stabilization on creep crack g
Effect of stabilization on creep crack growth in high-density polyethylene
✍ G. Pinter; R. W. Lang πŸ“‚ Article πŸ“… 2003 πŸ› John Wiley and Sons 🌐 English βš– 356 KB πŸ‘ 2 views

## Abstract Polyolefins, particularly polyethylene, are known to fail via crack initiation and crack propagation when exposed to multiaxial long‐term static stresses at elevated temperatures. Using concepts of linear elastic fracture mechanics, this article describes and discusses the effects of st

Stepwise fatigue crack propagation in po
Stepwise fatigue crack propagation in polyethylene resins of different molecular structure
✍ A. Shah; E. V. Stepanov; G. Capaccio; A. Hiltner; E. Baer πŸ“‚ Article πŸ“… 1998 πŸ› John Wiley and Sons 🌐 English βš– 483 KB

Stepwise fatigue crack propagation in a range of polyethylene resins, some of which are candidates for use in pipes for natural gas distribution, was studied. Examination of the effect of molding conditions on fatigue crack propagation in a pipe resin indicated that fast cooling under pressure produ

Crack nucleation and propagation of corr
Crack nucleation and propagation of corrosion fatigue in high-strength steel
✍ Y Hirose; T Mura πŸ“‚ Article πŸ“… 1985 πŸ› Elsevier Science 🌐 English βš– 851 KB

Crack nucleation and growth behavior of corrosion fatigue are investigated experimentally and theoretically for 200Β°C tempered AISI 4340 steel in 35% NaCl solution. The crack nucleation at notch roots is determined by the electrical potential method. The cycle for crack nucleation, N,, increases wit

Fatigue crack propagation behavior of ul
Fatigue crack propagation behavior of ultra high molecular weight polyethylene under mixed mode conditions
✍ Elbert, K. E. ;Wright, T. M. ;Rimnac, C. M. ;Klein, R. W. ;Ingraffea, A. R. ;Gun πŸ“‚ Article πŸ“… 1994 πŸ› John Wiley and Sons 🌐 English βš– 609 KB

## Abstract Analytical studies of the stresses on and within ultra high molecular weight polyethylene joint components suggest that damage modes associated with polyethylene fatigue failure are caused by a combination of surface and subsurface crack propagation. Fatigue crack propagation tests unde