Three polypyrrole-silica nanocomposites were characterized by inverse gas chromatography (IGC) at 60 and 80degreesC using both linear and branched alkane probes. The IGC data for these materials were compared with those obtained for the ultrafine silica sol and polypyrrole (PPy) bulk powder reference materials. The London components of the surface energies (gammasd) of the nanocomposites were in the range 115-225 mJ m-2 at 60degreesC. These values are much higher than those obtained for either the polypyrrole powders or the colloidal silica sol, which suggests that the nanocomposites have significant microporosity. The gammasd values for the nanocomposites decrease in the order chloride-doped PPy > sulfate-doped PPy > tosylate-doped PPy, which is the same trend as that found for the heat of adsorption (DeltaHa) of a given n-alkane. DeltaHa values of the linear and branched alkanes are up to three times higher than the heats of vaporization, which confirms that the nanocomposites (and, to a lesser extent, the polypyrrole powders) have high adsorption capacities for these solutes. For a series of alkane isomers (e.g., C7H16 or C8H18), the difference between the DeltaHa values for the nanocomposites and the corresponding polypyrrole powders decreased as the degree of branching for these probes was increased. These observations suggest that the more sterically hindered probes are excluded from the microporous interior of the nanocomposites. Copyright 1997 Academic Press. Copyright 1997Academic Press
📜 SIMILAR VOLUMES
Partial esterification of cellulose using acyl chlorides having 5 and 16 carbon atoms was performed in a swelling medium to produce cellulosic esters with two different degrees of substitution (DS Å 0.15 and 0.45). The effects of this treatment on the surface energy, on the water uptake, and on the
## Abstract Inverse gas chromatography (IGC) studies on the surface of polyethylene (PE) particles grafted with acrylic acid and acryl amide have been reported. Surface properties of the virgin and grafting‐modified PE were compared by IGC. The dispersive contributions of the surface free energy γ