8. Catalysis of the graphitization of some carbons by chromium

โœ Scribed by J Gillot; B Lux; P Cornuault; F du Chaffaut

Publisher
Elsevier Science
Year
1969
Tongue
English
Weight
132 KB
Volume
7
Category
Article
ISSN
0008-6223

No coin nor oath required. For personal study only.

โœฆ Synopsis

resin binders with the intent of using the experimental results as a guide to improve graphite fabrication. Experimental data directed towards an understanding of the relationships between DTA and fabrication variables are reported.

๐Ÿ“œ SIMILAR VOLUMES

Catalytic graphitization of graphitizabl
Catalytic graphitization of graphitizable carbon by chromium, manganese and molybdenum oxides
โœ Isao Mochida; Ryosuke Ohtsubo; Kenjiro Takeshita; Harry Marsh ๐Ÿ“‚ Article ๐Ÿ“… 1980 ๐Ÿ› Elsevier Science ๐ŸŒ English โš– 426 KB

Catalytic graphitization of a graphitizable carbon from Kureha pitch is investigated in the temperature range 1200-2800 K, using chromia and other chromium compounds. Two distinct stages of catalytic graphitization are detected at temperatures of 1500-1800 K and above 2000 K. Values of Lc(002) and 6

Effect of oxidation on the surface heter
Effect of oxidation on the surface heterogeneity of some graphitized carbons
โœ D.W.L Griffiths; W.J Thomas; P.L Walker Jr. ๐Ÿ“‚ Article ๐Ÿ“… 1964 ๐Ÿ› Elsevier Science ๐ŸŒ English โš– 860 KB

fraction of the surface of some graphitized carbons are energetically heterogeneous. That part of the surface which is heterogeneous has sites for which N, shows a higher isosteric heat of adsorption at 78ยฐK than the uniform portion constituting the major fraction of surface and for which the heat o

Effect of oxidation on the pore structur
Effect of oxidation on the pore structure of some graphitized carbon blacks
โœ W.J Thomas ๐Ÿ“‚ Article ๐Ÿ“… 1966 ๐Ÿ› Elsevier Science ๐ŸŒ English โš– 801 KB

The effect of oxidation on the pore structure of two different graphitized carbons has been investigated. Graphon and P33 were subjected to oxidation to achieve various extents of bum-off and the pore structure of each sample was subsequently examined using the techniques of low temperature adsorpti