The spontaneous passivation behaviour of a Fe-22Cr-3Mo-5Ni alloy system containing small amounts of ruthenium in 0.5 M HCI solution has been investigated by means of immersion tests, electrochemical measurements and the XPS technique.The weight loss and electrochemical measurements show that increasing amounts of ruthenium (up to 0.3 wt%) in Fe-22Cr-3Mo-5Ni substantially improve resistance to attack by hydrochloric acid.'The XPS results show that the spontaneously formed passive film on this alloy with ruthenium mainly consists of Cr and Mo oxyhydroxides. Molybdenum is incorporated as Mo4+ and Mo6+, while neither ruthenium nor nickel are found in the passive film. The effects of ruthenium additions on the spontaneous passivation of FeCrMoNi alloys are discussed.
Mit Hilfe von
Gewichtsverlust-Messungen, elektrochemischen Messungen und der XPS-Technik wird die spontane Passivierung einer Fe-22Cr-3Mo-SNi-Legierung mit geringen Zusatzen von Ruthenium in 0,5 M HCI untersucht. Die Gewichtsverluste sowie die Ergebnisse der elektrochemischen Messungen zeigen, daB zunehmende Rutheniummengen (bis 0,3 Gew%) den Widerstand der Legierung gegen Salzsaure erheblich verbessern. Die Ergebnisse der XPS-Messungen zeigen wiederum, daB die spontan gebildete Passivierungsschicht auf dieser Ru-haltigen Legierung hauptsachlich aus Cr-und Mo-Oxyhydroxid besteht. Ferner wurde festgestellt, daD die Passivschicht weder Ruthenium noch Nickel enthalt . Die Auswirkung von kathodischen Legierungszusatzen wie Ru auf die spontane Passivierung der FeCrMoNi-Legierung wird erortert.