Abstract
To precisely identify the effect of blend ratios of syndiotacticity‐rich poly(vinyl alcohol) (s‐PVA)/atactic PVA (a‐PVA) on the water stability of s‐PVA/a‐PVA/iodine complex blend films, we prepared two PVAs with similar number‐averaged degrees of polymerization of 4000 and degrees of saponification of 99.9% and with different syndiotactic diad contents of 58.5 and 53.5%, respectively. The desorption behavior of iodine in s‐PVA/a‐PVA/iodine complex films in water was investigated in terms of the solubility of s‐PVA/a‐PVA blend films in water. The degree of solubility of s‐PVA/a‐PVA blend films with s‐PVA content over 50% in water at 70°C was limited to about 10–20%, whereas that of s‐PVA/a‐PVA blend films with s‐PVA content of 10% was 85% under the same conditions. The degree of iodine desorption of complex blend films decreased with increasing s‐PVA content. The degree of iodine desorption of s‐PVA/a‐PVA drawn film with s‐PVA content of 90% was limited to 7%, regardless of the soaking temperature from 30 to 70°C. The desorption of iodine in water was strongly affected by the dissolution of blends. Moreover, the stability of iodine in the drawn s‐PVA/a‐PVA/iodine blend films in hot water was far superior to that of the undrawn film. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 94: 1435–1439, 2004