Viscoelasticity of low molecular weight polystyrene. Separation of rubbery and glassy components

✍ Scribed by Tadashi Inoue; Takayuki Onogi; Ming-Long Yao; Kunihiro Osaki

• Publisher: John Wiley and Sons
• Year: 1999
• Tongue: English
• Weight: 191 KB
• Volume: 37
• Category: Article
• ISSN: 0887-6266
• DOI: 10.1002/(sici)1099-0488(19990215)37:4<389::aid-polb12>3.0.co;2-g

✦ Synopsis

The complex shear modulus was measured for four low molecular-weight polystyrenes (M w ϭ 10,500, 5970, 2630, and 1050) near and above the glass transition temperature. For the lowest molecular weight sample, the method of reduced variables, the time-temperature superposition principle, was applicable, while it was not applicable for the higher M samples. For these higher M samples, it was assumed that the complex modulus is composed of two components (R and G components). The R component was estimated by subtracting the G component, which was assumed to be the same as the modulus of the lowest molecular weight sample. The time-temperature superposition principle was applicable to each of the R and G components, and the shift factors were different from each other. The contribution of the R component to the total complex modulus decreased with decreasing M. Anomalous temperature dependence of the steady-state compliance for low M polymers as Plazek reported could be attributed to difference in temperature dependence of the two components. The estimated complex modulus for the R component was in accord with that calculated by spring-bead model theory.