Abstract
Summary: Functionalized metallocene copolymers synthesized from ethylene with 5‐hexen‐1‐ol and ethylene with 10‐undecen‐1‐ol were used as compatibilizers in LDPE/starch and LDPE/dextran blends in order to improve the interfacial adhesion between hydrophobic LDPE and hydrophilic natural polymers. An increase in tensile modulus and a slight decrease in tensile strength was observed when poly[ethylene‐co‐(10‐undecen‐1‐ol)] was added to a 70:30 wt.‐% LDPE/dextran blend, whereas the addition of poly[ethylene‐co‐(5‐hexen‐1‐ol)] as compatibilizer resulted in obtaining a more rigid material with a slightly higher modulus. Scanning electron microscopy of modified dextran blends containing 3 wt.‐% of both compatibilizers showed some degree of phase cocontinuity. Enhanced interfacial adhesion and decrease in particle size of starch was observed when 5 wt.‐% of poly [ethylene‐co‐(5‐hexen‐1‐ol)] copolymer was used as the compatibilizer in starch blends. The crystallization temperature of LDPE, determined by DSC, was shifted to a slightly higher temperature as a consequence of the addition of the compatibilizers. The existence of phase segregation was also revealed by thermal analysis when 5 wt.‐% of the copolymers were used as blend modifiers.
SEM micrograph of 70:30 wt.‐% LDPE/dextran blend with added poly[ethylene‐co‐(5‐hexen‐1‐ol)] compatibilizer.
magnified imageSEM micrograph of 70:30 wt.‐% LDPE/dextran blend with added poly[ethylene‐co‐(5‐hexen‐1‐ol)] compatibilizer.