Triple point crack growth in an age hardened aluminium-20% zinc alloy
✍ Scribed by J.A Williams
- Publisher
- Elsevier Science
- Year
- 1967
- Weight
- 366 KB
- Volume
- 15
- Category
- Article
- ISSN
- 0001-6160
No coin nor oath required. For personal study only.
✦ Synopsis
The growth of triple point cracks has been studied at 200°C and 3000-5000 psi in an aluminium-2Oq', zinc alloy heat treated t,o give a 4 p wide precipitate free zone at the grain boundaries. The cracks are shown to exhibit a stable growth stage before instabilit,y occurs and the appropriate effective fracture surface energy is l-2 x lo5 ergs/cm*. Using the instability criterion, good agreement is obtained between calculated and experimental fracture lives. CROISSANCE DE FISSURES A UK POIKT TRIPLE DAnTS UK ALLIAGE ALTTMIKIUM-209; ZINC DURCI PAR VIEILLISSEMEn'T On a Btudib la croissance de fissures I un point triple iL 200°C et 3000-5000 psi dans un alliage aluminium 20qb zinc oti un traitement thermique donne aux joints de grains une zone sane p&ipiti de 4 p. Les fissures montrent un stade de croissance stable avant l'instabilit6 et 1'6nergie superficielle de rupture efficace est l-2 x lo1 ergs/cm*. En utilisant le &t&e d'instabiliti, on obtient un bon accord entre les vale;lrs calcu&es et expbrimentales du temps de rupture. WACHSTUM VOn-DREIPUI'KTRISSEP; Ih' EIn-ER GEALTERTEN ALUMINIUM-SOO/b ZIn'K-LEGIERUNG Des Wachsen van Dreipunktrissen wurde bei 200°C und 3000-5000 psi in einer Aluminium-200,b Zink-Legierung untersucht, die so wllrmebehandelt war, dass eine 4 y breite ausscheidungsfreie Zone an den Korngrenzen entstand. Die Risse zeigen ein sta,biies Wachstumstadium, bevor die Instabilitiit beginnt. Die entaprechende effektive Bruchoberflilchenenergie ist 1-2 x lo5 erg/cm*. Kach dem Instabilitiitskriterium besteht' gute ubereinstimmung zwischen berechneten und experiment&en Lebensdauera bis zum Bruch.